General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 14.49 g/cm³ Show Supplier Material materials with Density of 14.49 g/cm³ | |
Grain size | 0.8 - 1.3 μm Show Supplier Material materials with Grain size of 0.8 - 1.3 μm | tungsten carbide grain size | |
Particle size D90 | 16 μm Show Supplier Material materials with Particle size D90 of 16 μm | max |
Mechanical
Property | Temperature | Value |
---|---|---|
Hardness, Vickers, 30 | 23.0 °C | 1560 [-] Show Supplier Material materials with Hardness, Vickers, 30 of 1560 [-] |
Magnetic
Property | Temperature | Value |
---|---|---|
Coercive force | 23.0 °C | 19104 A/m Show Supplier Material materials with Coercive force of 19104 A/m |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Aluminium | 0.02 % Show Supplier Material materials with Aluminium of 0.02 % | max | |
Carbon | as WC balance | ||
Chromium | 0.6 % Show Supplier Material materials with Chromium of 0.6 % | max | |
Cobalt | 8 - 12 % Show Supplier Material materials with Cobalt of 8 - 12 % | ||
Copper | 0.02 % Show Supplier Material materials with Copper of 0.02 % | max | |
Iron | 0.3 % Show Supplier Material materials with Iron of 0.3 % | max | |
Nickel | 0.1 % Show Supplier Material materials with Nickel of 0.1 % | max | |
Niobium | 0.1 % Show Supplier Material materials with Niobium of 0.1 % | max | |
Oxygen | 0.3 % Show Supplier Material materials with Oxygen of 0.3 % | max | |
Tantalum | 0.1 % Show Supplier Material materials with Tantalum of 0.1 % | max | |
Titanium | 0.1 % Show Supplier Material materials with Titanium of 0.1 % | max | |
Tungsten | as WC balance | ||
Vanadium | 0.2 % Show Supplier Material materials with Vanadium of 0.2 % | max | |
Zinc | 5E-3 % Show Supplier Material materials with Zinc of 5E-3 % | max |
Technological properties
Property | ||
---|---|---|
Application areas | Powder grade F was developed for use in a wide range of tooling products, such as hardmetal rods, indexable inserts, woodworking tools and wear parts. | |
Other | Grade F powder exhibits a unifrom WC grain size distribution with evenly distributed WC and Cobalt particles. Thanks to the fine particle size of the powder, milling characteristics are great and comparable to virgin WC-Co powders. |