Mechanisch
Property | Value | Comment |
---|---|---|
Dehnung | 16 % Show Supplier Material materials with Dehnung of 16 % | min. | for thickness 0.65 mm | Transverse | A80 | Guaranteed |
30 - 40 % Show Supplier Material materials with Dehnung of 30 - 40 % | for thickness 0.65 mm | Transverse | A80 | Typical values | |
Härte, Vickers | 120 - 150 [-] Show Supplier Material materials with Härte, Vickers of 120 - 150 [-] | Typical values for thickness 0.65 mm |
Streckgrenze | 250 MPa Show Supplier Material materials with Streckgrenze of 250 MPa | min. | Guaranteed | Transverse |
270 - 320 MPa Show Supplier Material materials with Streckgrenze of 270 - 320 MPa | Typical values | Transverse | |
Yield to strength ratio | 0.68 - 0.73 [-] Show Supplier Material materials with Yield to strength ratio of 0.68 - 0.73 [-] | Typical values |
Zugfestigkeit | 325 MPa Show Supplier Material materials with Zugfestigkeit of 325 MPa | min. | Guaranteed |
400 - 440 MPa Show Supplier Material materials with Zugfestigkeit of 400 - 440 MPa | Typical values |
Magnetisch
Property | Value | Comment |
---|---|---|
Garantierte Polarisierung | 1.6 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.6 [-] | min. | for thickness 0.65 mm | in DC at 5000 A/m |
1.83 [-] Show Supplier Material materials with Garantierte Polarisierung of 1.83 [-] | min. | for thickness 0.65 mm | in DC at 15000 A/m | |
Typische Polarisierung | 1.72 [-] Show Supplier Material materials with Typische Polarisierung of 1.72 [-] | min. | for thickness 0.65 mm | in DC at 5000 A/m |
1.91 [-] Show Supplier Material materials with Typische Polarisierung of 1.91 [-] | min. | for thickness 0.65 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |