Eigenschaften
Allgemein
| Property | Temperature | Value | |
|---|---|---|---|
Dichte | 23.0 °C | 15.05 g/cm³ Show Supplier Material materials with Dichte of 15.05 g/cm³ | |
Kornstruktur | Ultrafine (0,2µm - 0,5µm) | ||
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastizitätsmodul | 23.0 °C | 646 GPa Show Supplier Material materials with Elastizitätsmodul of 646 GPa | |
Härte, Rockwell A | 23.0 °C | 94.6 [-] Show Supplier Material materials with Härte, Rockwell A of 94.6 [-] | |
Härte, Vickers, 10 | 23.0 °C | 2300 [-] Show Supplier Material materials with Härte, Vickers, 10 of 2300 [-] | EN ISO 6507-1 |
Härte, Vickers, 30 | 23.0 °C | 2200 [-] Show Supplier Material materials with Härte, Vickers, 30 of 2200 [-] | EN ISO 6507-1 |
Plane-Strain Fracture Toughnes | 23.0 °C | 8.4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 8.4 MPa·√m | ISO 28079 |
Poissonzahl | 23.0 °C | 0.2 [-] Show Supplier Material materials with Poissonzahl of 0.2 [-] | |
Zugfestigkeit, transversal | 23.0 °C | 3700 MPa Show Supplier Material materials with Zugfestigkeit, transversal of 3700 MPa | DIN EN ISO 7438 |
Thermisch
| Property | Temperature | Value |
|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.62E-6 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.62E-6 1/K |
Spezifische Wärmekapazität | 23.0 °C | 0.19 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 0.19 J/(kg·K) |
Temperaturleitfähigkeit | 23.0 °C | 21.3 mm²/s Show Supplier Material materials with Temperaturleitfähigkeit of 21.3 mm²/s |
Wärmeleitfähigkeit | 23.0 °C | 59 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 59 W/(m·K) |
Chemical properties
Technological properties
| Property |
|---|