| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.18 g/cm³ Show Supplier Material materials with Dichte of 1.18 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 140 MPa Show Supplier Material materials with Biegefestigkeit of 140 MPa | ISO 178 (2mm/min) |
Biegemodul | 23.0 °C | 4.2 GPa Show Supplier Material materials with Biegemodul of 4.2 GPa | ISO 178 (2mm/min) |
Dehnung | 23.0 °C | 6 % Show Supplier Material materials with Dehnung of 6 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 5.1 GPa Show Supplier Material materials with Elastizitätsmodul of 5.1 GPa | ISO 527-2 (1mm/min) |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 6 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 6 kJ/m² | ISO 180/1A |
23.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 13 kJ/m² | ISO 180/1A | |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 65 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 65 kJ/m² | ISO 180/1U |
Zugfestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa | ISO 527-2 (5mm/min) |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 14 % Show Supplier Material materials with Aschegehalt of 14 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 240 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 230 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 230 °C | ISO 75-2/A | |||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB EN 60695-11-10 | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Eplamid 66 glass fiber and impact modified grades are used in all sectors of industry, offering a good impact strength for mechanical properties and ensures an outstanding performance even at low temperatures (up to -40°C). | |
| Fillers | 14% Glass Fiber | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |