Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Dichte of 1.35 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.2 % Show Supplier Material materials with Water content of 0.2 % | ISO 15512 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 285 MPa Show Supplier Material materials with Biegefestigkeit of 285 MPa | ISO 178 (2mm/min) |
Biegemodul | 23.0 °C | 8.7 GPa Show Supplier Material materials with Biegemodul of 8.7 GPa | ISO 178 (2mm/min) |
Dehnung | 23.0 °C | 3.5 % Show Supplier Material materials with Dehnung of 3.5 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 9.5 GPa Show Supplier Material materials with Elastizitätsmodul of 9.5 GPa | ISO 527-2 (1mm/min) |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 12 kJ/m² | ISO 180/1A |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 70 kJ/m² | ISO 180/1U |
Zugfestigkeit | 23.0 °C | 185 MPa Show Supplier Material materials with Zugfestigkeit of 185 MPa | ISO 527-2 (5mm/min) |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 30 % Show Supplier Material materials with Aschegehalt of 30 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 225 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 225 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 215 °C | ISO 75-2/A | |||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 glass fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties. | |
Fillers | 30% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |