Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.13 g/cm³ Show Supplier Material materials with Dichte of 1.13 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 90 MPa Show Supplier Material materials with Biegefestigkeit of 90 MPa | ISO 178 (2mm/min) | ||
Biegemodul | 23.0 °C | 2.8 GPa Show Supplier Material materials with Biegemodul of 2.8 GPa | ISO 178 (2mm/min) | ||
Dehnung | 23.0 °C | 15 % Show Supplier Material materials with Dehnung of 15 % | ISO 527-2 (5mm/min) | ||
Elastizitätsmodul | 23.0 °C | 3.2 GPa Show Supplier Material materials with Elastizitätsmodul of 3.2 GPa | ISO 527-2 (1mm/min) | ||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 7 kJ/m² | ISO 180/1A | ||
Zugfestigkeit | 23.0 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | ISO 527-2 (5mm/min) | ||
Schlagzähigkeit, Charpy ungekerbt | no break at 23°C; ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | no break at 23°C; ISO 180/1U | ||||
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 220 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75-2/B | |
Heat deflection temperature, 1.80 MPa | 75 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ISO 75-2/A | |
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | ISO 3146 | |
Ball Pressure Test | <2, for 125+/-2°C, EN 60695-10-2 | ||
Entflammbarkeit | UL94 (0.8mm) V2 | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 550 V Show Supplier Material materials with Kriechstromfestigkeit of 550 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 120 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 120 cm³/10min | ISO 1133 (275°C/5 kg) | |
Schrumpfung | 23.0 °C | 1.4 % Show Supplier Material materials with Schrumpfung of 1.4 % | ISO 294-4 (3mm) |
Schrumpfung, diagonal | 23.0 °C | 1.6 % Show Supplier Material materials with Schrumpfung, diagonal of 1.6 % | ISO 294-4 (3mm) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Eplamid 66 offers all primary properties of unreinforced PA66 used in all sectos of industry, good balance of thermal and mechanical properties, especially for thin wall and fast cycle applications. | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |