Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.45 g/cm³ Show Supplier Material materials with Dichte of 1.45 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 105 MPa Show Supplier Material materials with Biegefestigkeit of 105 MPa | ISO 178 (2mm/min) |
Biegemodul | 23.0 °C | 3.5 GPa Show Supplier Material materials with Biegemodul of 3.5 GPa | ISO 178 (2mm/min) |
Dehnung | 23.0 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 3.8 GPa Show Supplier Material materials with Elastizitätsmodul of 3.8 GPa | ISO 527-2 (1mm/min) |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 30 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 3 kJ/m² | ISO 180/1A |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 25 kJ/m² | ISO 180/1U |
Zugfestigkeit | 23.0 °C | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | ISO 527-2 (5mm/min) |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 20 % Show Supplier Material materials with Aschegehalt of 20 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 205 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 75 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 75 °C | ISO 75-2/A | |||
Schmelzpunkt | 225 °C Show Supplier Material materials with Schmelzpunkt of 225 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 250 V Show Supplier Material materials with Kriechstromfestigkeit of 250 V | EN 60112 |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+13 Ω/sq | ASTM D257 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | EPIMIX PBT glass bead reinforced grades are used in all sectors of industry, has and excellent surface finish, low warpage and all around excellent mechanical properties. | |
| Fillers | 20% Glass Bead | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |