Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.52 g/cm³ Show Supplier Material materials with Dichte of 1.52 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 14.7 GPa Show Supplier Material materials with Elastizitätsmodul of 14.7 GPa | ISO 527-2 (1mm/min) |
Hardness, Ball Indentation | 23.0 °C | 310 MPa Show Supplier Material materials with Hardness, Ball Indentation of 310 MPa | ISO 2039-1 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 220 MPa Show Supplier Material materials with Zugfestigkeit of 220 MPa | ISO 527-2 (5mm/min) |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 40 % Show Supplier Material materials with Aschegehalt of 40 % | ISO 3451-4 | ||
Heat deflection temperature, 1.80 MPa | 280 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 280 °C | ISO 75-2/A | |||
Heat deflection temperature, 8.0 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 175 °C | ISO 75-2/B | |||
Max. Betriebstemperatur, kurz | 250 °C Show Supplier Material materials with Max. Betriebstemperatur, kurz of 250 °C | ISO 2578 | |||
Max. Betriebstemperatur, lang | 140 °C Show Supplier Material materials with Max. Betriebstemperatur, lang of 140 °C | ISO 2578 | |||
Schmelzpunkt | 315 °C Show Supplier Material materials with Schmelzpunkt of 315 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB |
Elektrisch
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid HT00 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required. | |
Fillers | 40% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |