Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.75 g/cm³ Show Supplier Material materials with Dichte of 1.75 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 1.5 % Show Supplier Material materials with Dehnung of 1.5 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 22 GPa Show Supplier Material materials with Elastizitätsmodul of 22 GPa | ISO 527-2 (1mm/min) |
Hardness, Ball Indentation | 23.0 °C | 330 MPa Show Supplier Material materials with Hardness, Ball Indentation of 330 MPa | ISO 2039-1 |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 12 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 265 MPa Show Supplier Material materials with Zugfestigkeit of 265 MPa | ISO 527-2 (5mm/min) |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 60 % Show Supplier Material materials with Aschegehalt of 60 % | ISO 3451-4 | ||
Heat deflection temperature, 1.80 MPa | 285 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 285 °C | ISO 75-2/A | |||
Heat deflection temperature, 8.0 MPa | 210 °C Show Supplier Material materials with Heat deflection temperature, 8.0 MPa of 210 °C | ISO 75-2/B | |||
Max. Betriebstemperatur, kurz | 250 °C Show Supplier Material materials with Max. Betriebstemperatur, kurz of 250 °C | ISO 2578 | |||
Max. Betriebstemperatur, lang | 150 °C Show Supplier Material materials with Max. Betriebstemperatur, lang of 150 °C | ISO 2578 | |||
Schmelzpunkt | 315 °C Show Supplier Material materials with Schmelzpunkt of 315 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB |
Elektrisch
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid HT00 grades are used for molding technical parts where higher operating temperatures and higher stiffness in moist environments are required. | |
Fillers | 60% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |