Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.27 g/cm³ Show Supplier Material materials with Dichte of 1.27 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 330 MPa Show Supplier Material materials with Biegefestigkeit of 330 MPa | ISO 178 (2mm/min) |
Biegemodul | 23.0 °C | 19 GPa Show Supplier Material materials with Biegemodul of 19 GPa | ISO 178 (2mm/min) |
Dehnung | 23.0 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | ISO 527-2 (5mm/min) |
Elastizitätsmodul | 23.0 °C | 21 GPa Show Supplier Material materials with Elastizitätsmodul of 21 GPa | ISO 527-2 (1mm/min) |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 48 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 48 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 38 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 38 kJ/m² | ISO 180/1U |
Zugfestigkeit | 23.0 °C | 220 MPa Show Supplier Material materials with Zugfestigkeit of 220 MPa | ISO 527-2 (5mm/min) |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Aschegehalt | 23.0 °C | 30 % Show Supplier Material materials with Aschegehalt of 30 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 195 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 195 °C | ISO 75-2/A | |||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | ISO 3146 | |||
Entflammbarkeit | UL94 (0.8mm) HB, EN 60695-11-10 | ||||
Elektrisch
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Eplamid 6 carbon fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties. | |
| Fillers | 30% Carbon Fiber | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |