Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 23.0 °C | 8.9 g/cm³ Show Supplier Material materials with Dichte of 8.9 g/cm³ |
Abmessung
| Property | Value |
|---|---|
Dimensions | Available size round products (mm): 1-20 |
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Dehnung | 23.0 °C | 3 % Show Supplier Material materials with Dehnung of 3 % |
Elastizitätsmodul | 23.0 °C | 124 GPa Show Supplier Material materials with Elastizitätsmodul of 124 GPa |
Härte, Brinell | 23.0 °C | 149 - 180 [-] Show Supplier Material materials with Härte, Brinell of 149 - 180 [-] |
Härte, Rockwell C | 23.0 °C | 0 - 10 [-] Show Supplier Material materials with Härte, Rockwell C of 0 - 10 [-] |
Härte, Vickers | 23.0 °C | 150 - 180 [-] Show Supplier Material materials with Härte, Vickers of 150 - 180 [-] |
Streckgrenze | 23.0 °C | 490 - 560 MPa Show Supplier Material materials with Streckgrenze of 490 - 560 MPa |
Zugfestigkeit | 23.0 °C | 550 - 700 MPa Show Supplier Material materials with Zugfestigkeit of 550 - 700 MPa |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.8E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K | for 20-200°C |
Wärmeleitfähigkeit | 23.0 °C | 244 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 244 W/(m·K) | for 20-200°C |
Elektrisch
| Property | Temperature | Value |
|---|---|---|
Elektrische Leitfähigkeit | 23.0 °C | 2.90E+7 S/m Show Supplier Material materials with Elektrische Leitfähigkeit of 2.90E+7 S/m |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Summary of typical applications: Connectors, spring contact. It is extensively used in industries like Aerospace, Automotive and Health equipment, and in many other fields requiring high performance and durability. | |
| Corrosion properties | Corrosion resistance rating: 4 out of 5 | |
| General machinability | Machinability: 70 % | |
| Processing history | Condition: H14 | |