| Property | Value |
|---|---|
Bound AN Content | 28.0 % Show Supplier Material materials with Bound AN Content of 28.0 % |
Dichte | 0.98 g/cm³ Show Supplier Material materials with Dichte of 0.98 g/cm³ |
Volatile share | 0.3 % Show Supplier Material materials with Volatile share of 0.3 % |
Mechanisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Dehnung | 510 % Show Supplier Material materials with Dehnung of 510 % | ASTM D412 | 145°C×50min. Cured |
Modul bei 300 % Dehnung | 0.02 GPa Show Supplier Material materials with Modul bei 300 % Dehnung of 0.02 GPa | ASTM D412 | 145°C×50min. Cured |
Zugfestigkeit | 250 MPa Show Supplier Material materials with Zugfestigkeit of 250 MPa | ASTM D412 | 145°C×50min. Cured |
Thermisch
| Property | Value | Comment |
|---|---|---|
Aschegehalt | 0.1 % Show Supplier Material materials with Aschegehalt of 0.1 % | max. |
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Mooney-Viskosität | 60 MU Show Supplier Material materials with Mooney-Viskosität of 60 MU | ML1+4 and 100°C |
Technological properties
| Property | ||
|---|---|---|
| Application areas | NBR 2860 is recommended for use in industrial and automotive parts such as packing, gasket and oil hose. | |
| Color | Light Tan | |
| Other | Shelf Life : 18 months from date of production atb room temperatures not exceeding 30°C under belowed storage condition (Retest critical parameters like MV and others after the expiry of shelf life). Storage condition: NBR should be stored in warehouse to be protected from sunlight, heat, moisture and foreign materials. | |
| Packaging size | Bale Weight: 35kg Bale wrapping film: LDPE | |
| Processing history | Polymerization: Cold Emulsion | |
| Processing methods | Recipe (ASTM D3187): NBR 2860: 100 phr HAF(IRB #8): 40 ZnO: 3.0 Stearic Acid: 1.0 TBBS: 0.7 Sulfur: 1.5 Total: 146.2 | |
| Stabilizer | Non-Staining | |