Allgemein
Property | Temperature | Value |
---|---|---|
Dichte | 23.0 °C | 8.81 g/cm³ Show Supplier Material materials with Dichte of 8.81 g/cm³ |
Abmessung
Property | Value |
---|---|
Breite | 1.27 - 406.5 mm Show Supplier Material materials with Breite of 1.27 - 406.5 mm |
Dicke | 0.05 - 0.38 mm Show Supplier Material materials with Dicke of 0.05 - 0.38 mm |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefähigkeit 90°, in longitudinaler Richtung | 23.0 °C | 5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 5 [-] | >10mm (2 for <10mm) |
Biegefähigkeit 90°, in transversaler Richtung | 23.0 °C | 5 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 5 [-] | >10mm (2 for <10mm) |
Dauerfestigkeit | 23.0 °C | 580 - 685 MPa Show Supplier Material materials with Dauerfestigkeit of 580 - 685 MPa | 10⁸ cycles R=0 (Unidirectional) |
Dehnung | 23.0 °C | 1 % Show Supplier Material materials with Dehnung of 1 % | in 25mm |
Elastizitätsmodul | 23.0 °C | 138 GPa Show Supplier Material materials with Elastizitätsmodul of 138 GPa | |
Härte, Vickers | 23.0 °C | 280 - 340 [-] Show Supplier Material materials with Härte, Vickers of 280 - 340 [-] | |
Streckgrenze Rp 0,2 | 23.0 °C | 930 - 1055 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 930 - 1055 MPa | |
Zugfestigkeit | 23.0 °C | 950 - 1090 MPa Show Supplier Material materials with Zugfestigkeit of 950 - 1090 MPa |
Thermisch
Property | Value |
---|---|
Schmelzpunkt | 1030 °C Show Supplier Material materials with Schmelzpunkt of 1030 °C |
Elektrisch
Property | Value | Comment |
---|---|---|
Specific Electrical conductivity | 44 % IACS Show Supplier Material materials with Specific Electrical conductivity of 44 % IACS | nominal value |
Chemical properties
Property | Value |
---|---|
Beryllium | 0.15 - 0.5 % Show Supplier Material materials with Beryllium of 0.15 - 0.5 % |
Kupfer | Balance |
Nickel | 1 - 1.4 % Show Supplier Material materials with Nickel of 1 - 1.4 % |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include power contacts and burn-in and test socket contacts. |