Eigenschaften
Allgemein
| Property | Temperature | Value |
|---|---|---|
Dichte | 23.0 °C | 9 g/cm³ Show Supplier Material materials with Dichte of 9 g/cm³ |
Abmessung
| Property | Value |
|---|---|
Durchmesser | 41 - 330 mm Show Supplier Material materials with Durchmesser of 41 - 330 mm |
Mechanisch
| Property | Temperature | Value |
|---|---|---|
Dehnung | 23.0 °C | 5 - 10 % Show Supplier Material materials with Dehnung of 5 - 10 % |
Elastizitätsmodul | 23.0 °C | 144 GPa Show Supplier Material materials with Elastizitätsmodul of 144 GPa |
Härte, Rockwell C | 23.0 °C | 30 [-] Show Supplier Material materials with Härte, Rockwell C of 30 [-] |
Poissonzahl | 23.0 °C | 0.33 [-] Show Supplier Material materials with Poissonzahl of 0.33 [-] |
Streckgrenze Rp 0,2 | 23.0 °C | 760 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 760 MPa |
Zugfestigkeit | 23.0 °C | 895 MPa Show Supplier Material materials with Zugfestigkeit of 895 MPa |
Thermisch
| Property | Temperature | Value |
|---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.64E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.64E-5 1/K |
Wärmeleitfähigkeit | 23.0 °C | 38 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 38 W/(m·K) |
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elektrische Leitfähigkeit | 23.0 °C | 4.00E+6 S/m Show Supplier Material materials with Elektrische Leitfähigkeit of 4.00E+6 S/m | max. |
Specific Electrical conductivity | 7 % IACS Show Supplier Material materials with Specific Electrical conductivity of 7 % IACS | max. |
Magnetisch
| Property | Temperature | Value |
|---|---|---|
Relative magnetische Permeabilität | 23.0 °C | 1 [-] Show Supplier Material materials with Relative magnetische Permeabilität of 1 [-] |
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | ToughMet 3 AT alloy is used for bushings and bearings for commercial aircraft, high performance engines as well as mining, industrial and heavy equipment. It is also used to make oil and gas drilling hardware, including rotary steerable housings, kelly valve seats and pressure housings. | |
| Surface Finish | Mill hardened finish | |