Allgemein
Property | Temperature | Value |
---|---|---|
Dichte | 23.0 °C | 8.27 g/cm³ Show Supplier Material materials with Dichte of 8.27 g/cm³ |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 9 % Show Supplier Material materials with Dehnung of 9 % | min., for strip thicker than 0.10 mm |
Elastizitätsmodul | 23.0 °C | 195 - 210 GPa Show Supplier Material materials with Elastizitätsmodul of 195 - 210 GPa | |
Hardness, Rockwell Superficial 15-N | 23.0 °C | 81 - 90 [-] Show Supplier Material materials with Hardness, Rockwell Superficial 15-N of 81 - 90 [-] | |
Härte, Vickers | 23.0 °C | 395 - 695 [-] Show Supplier Material materials with Härte, Vickers of 395 - 695 [-] | |
Streckgrenze Rp 0,2 | 23.0 °C | 1380 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 1380 MPa | |
Zugfestigkeit | 23.0 °C | 1690 MPa Show Supplier Material materials with Zugfestigkeit of 1690 MPa | min. |
Thermisch
Property | Temperature | Value |
---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.45E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.45E-5 1/K |
Schmelzpunkt | 1195 - 1325 °C Show Supplier Material materials with Schmelzpunkt of 1195 - 1325 °C | |
Wärmeleitfähigkeit | 23.0 °C | 48 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 48 W/(m·K) |
Elektrisch
Property | Temperature | Value |
---|---|---|
Specific Electrical conductivity | 6 % IACS Show Supplier Material materials with Specific Electrical conductivity of 6 % IACS | |
spezifischer Widerstand | 23.0 °C | 2.8E-7 Ω·m Show Supplier Material materials with spezifischer Widerstand of 2.8E-7 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Some applications for this alloy are Belleville washers for fire protection sprinkler heads, thermostats, bellows, diaphragms, connectors and burn-in and test sockets electrical /electronic systems. | |
Plating | Alloy 360 strip when properly cleaned exhibits surface chemistry characteristics similar to other commercial nickel base alloys. Techniques and procedures for plating and joining commercial nickel base alloys can be used on nickel beryllium. |