Property | Temperature | Value |
---|---|---|
Dichte | 23.0 °C | 8.27 g/cm³ Show Supplier Material materials with Dichte of 8.27 g/cm³ |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefähigkeit 90°, in longitudinaler Richtung | 23.0 °C | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in longitudinaler Richtung of 0 [-] | |
Biegefähigkeit 90°, in transversaler Richtung | 23.0 °C | 0 [-] Show Supplier Material materials with Biegefähigkeit 90°, in transversaler Richtung of 0 [-] | |
Dehnung | 23.0 °C | 14 % Show Supplier Material materials with Dehnung of 14 % | min., for strip thicker than 0.10 mm |
Elastizitätsmodul | 23.0 °C | 195 - 210 GPa Show Supplier Material materials with Elastizitätsmodul of 195 - 210 GPa | |
Streckgrenze Rp 0,2 | 23.0 °C | 690 - 860 MPa Show Supplier Material materials with Streckgrenze Rp 0,2 of 690 - 860 MPa | |
Zugfestigkeit | 23.0 °C | 1070 - 1240 MPa Show Supplier Material materials with Zugfestigkeit of 1070 - 1240 MPa |
Thermisch
Property | Temperature | Value |
---|---|---|
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.45E-5 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.45E-5 1/K |
Schmelzpunkt | 1195 - 1325 °C Show Supplier Material materials with Schmelzpunkt of 1195 - 1325 °C | |
Wärmeleitfähigkeit | 23.0 °C | 48 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 48 W/(m·K) |
Elektrisch
Property | Temperature | Value |
---|---|---|
Specific Electrical conductivity | 5 % IACS Show Supplier Material materials with Specific Electrical conductivity of 5 % IACS | |
spezifischer Widerstand | 23.0 °C | 3.45E-7 Ω·m Show Supplier Material materials with spezifischer Widerstand of 3.45E-7 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Some applications for this alloy are Belleville washers for fire protection sprinkler heads, thermostats, bellows, diaphragms, connectors and burn-in and test sockets electrical /electronic systems. | |
Plating | Alloy 360 strip when properly cleaned exhibits surface chemistry characteristics similar to other commercial nickel base alloys. Techniques and procedures for plating and joining commercial nickel base alloys can be used on nickel beryllium. | |
Workability | Excellent - Used for deep-drawn and severely cupped or formed parts; can be bent flat through 180° angle in any direction |