Allgemein
Property | Value | Comment |
---|---|---|
Bonding strength | 816.46 Kg Show Supplier Material materials with Bonding strength of 816.46 Kg | Condition A |
Dichte | 1.89 g/cm³ Show Supplier Material materials with Dichte of 1.89 g/cm³ | |
Moisture absorption | 0.2 % Show Supplier Material materials with Moisture absorption of 0.2 % | Condition D₁-24/23 |
Mechanisch
Property | Value | Testing Standard | Comment |
---|---|---|---|
Biegefestigkeit | 289 MPa Show Supplier Material materials with Biegefestigkeit of 289 MPa | ASTM D790 | Condition E-1/150: T-150, Transverse |
315 MPa Show Supplier Material materials with Biegefestigkeit of 315 MPa | ASTM D790 | Condition E-1/150: T-150 | |
365.4 MPa Show Supplier Material materials with Biegefestigkeit of 365.4 MPa | ASTM D790 | Condition A, Transverse | |
472.3 MPa Show Supplier Material materials with Biegefestigkeit of 472.3 MPa | ASTM D790 | Condition A | |
Druckfestigkeit | 497.1 MPa Show Supplier Material materials with Druckfestigkeit of 497.1 MPa | Condition A | Flatwise | |
Härte, Rockwell M | 108 [-] Show Supplier Material materials with Härte, Rockwell M of 108 [-] | ||
Impact strength, Izod notched, ASTM | 549.8 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 549.8 J/m | Condition E-48/50, Transverse | |
667.2 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 667.2 J/m | Condition E-48/50 | ||
Scherfestigkeit | 173.7 MPa Show Supplier Material materials with Scherfestigkeit of 173.7 MPa | Transverse | |
Zugfestigkeit | 326.1 MPa Show Supplier Material materials with Zugfestigkeit of 326.1 MPa |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Glasübergangstemperatur | 180 °C Show Supplier Material materials with Glasübergangstemperatur of 180 °C | min. | DMA | |
Arc resistance | 185 seconds, ASTM D495, Condition A | ||
Entflammbarkeit | UL 94, Class V-0 |
Elektrisch
Property | Value | Frequency | Comment |
---|---|---|---|
Dielektrizitätskonstante | 4.1 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4.1 [-] | 1MHz | Condition D₁-24/23 |
Durchschlagfestigkeit | 26.77 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 26.77 kV/mm | Condition D-48/50 | |
29.92 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 29.92 kV/mm | Condition A | ||
Durchschlagspannung | 69 kV Show Supplier Material materials with Durchschlagspannung of 69 kV | Condition A | |
Verlustfaktor | 0.018 [-] Show Supplier Material materials with Verlustfaktor of 0.018 [-] | 1MHz | Condition D-24/23 |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications include electrical equipment subjected to elevated temperatures. | |
Fillers | Glass Fabric | |
Other | The mechanical properties are converted from American unit system to International unit system. | |
Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. |