Eigenschaften
Allgemein
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Dichte | 1.42 g/cm³ Show Supplier Material materials with Dichte of 1.42 g/cm³ | dry | ISO 1183 | |||
Moisture absorption | 23 °C | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | 50%RH | ISO 62 | 2 mm | |
Wasserabsorption | 1.1 % Show Supplier Material materials with Wasserabsorption of 1.1 % | ISO 62 | 2 mm | 24h immersion at 23°C | ||
2 % Show Supplier Material materials with Wasserabsorption of 2 % | ISO 62 | 1mm |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegefestigkeit | 310 MPa Show Supplier Material materials with Biegefestigkeit of 310 MPa | dry | ISO 178 | 2mm/min | |
Biegemodul | 11 GPa Show Supplier Material materials with Biegemodul of 11 GPa | dry | ISO 178 | 2mm/min | |
Dehnung | 3 % Show Supplier Material materials with Dehnung of 3 % | dry | ISO 527-2/1A | 5mm/min | |
Elastizitätsmodul | 11.5 GPa Show Supplier Material materials with Elastizitätsmodul of 11.5 GPa | dry | ISO 527-2/1A | 1mm/min | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 79 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 79 kJ/m² | dry | ISO 179/1eU | 23°C | |
Schlagzähigkeit, Izod ungekerbt | 23 °C | 14 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Izod ungekerbt of 14 kJ/m² | dry | ISO 180/1U | |
Zugfestigkeit | 210 MPa Show Supplier Material materials with Zugfestigkeit of 210 MPa | dry | ISO 527-2/1A | 5mm/min |
Thermisch
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 261 °C Show Supplier Material materials with Schmelzpunkt of 261 °C | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 250 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 250 °C | ISO 75/2Af | 1.80 MPa | ||
260 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 260 °C | ISO 75/2Bf | 0.45 MPa | |||
Entflammbarkeit | Thickness tested (mm): 0.8, Class: HB, Standard: UL 94 | Automotive Interior Flammability(mm/min): <100,method: ISO 3795 and thickness tested (mm): 2 | ||||
Technological properties
| Property | ||
|---|---|---|
| Additives | Release agent | |
| Certifications | RoHS 2011/65/UE | |
| Color | Black | |
| Features | Heat Stabilized | |
| Fillers | 35% Glass Fiber | |
| Processing methods | Injection Molding | |