Eigenschaften
Abmessung
| Property | Value |
|---|---|
Dicke | 0.03 - 0.04 mm Show Supplier Material materials with Dicke of 0.03 - 0.04 mm |
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 20.0 °C | 0.7 g/cm³ Show Supplier Material materials with Dichte of 0.7 g/cm³ | |
Filmstärke | 20.0 °C | 35.7 - 57.1 m²/kg Show Supplier Material materials with Filmstärke of 35.7 - 57.1 m²/kg | |
Oberflächendichte | 20.0 °C | 1.75E-3 - 2.8E-3 g/cm² Show Supplier Material materials with Oberflächendichte of 1.75E-3 - 2.8E-3 g/cm² | |
Schrumpfung | 120.0 °C | 4 % Show Supplier Material materials with Schrumpfung of 4 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Schrumpfung, diagonal | 120.0 °C | 2 % Show Supplier Material materials with Schrumpfung, diagonal of 2 % | GOST 18616, ISO 11501, ASTM D1204 (Thermal shrinkage at 120˚C, 5 min) |
Materialinformationen
| Property | Value |
|---|---|
Abmessung | Available thicknesses: 25, 30, 35, 40µm. |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 20.0 °C | 200 % Show Supplier Material materials with Dehnung of 200 % | GOST 14236, ISO 527, ASTM D882 |
Dehnung, transversal | 20.0 °C | 60 % Show Supplier Material materials with Dehnung, transversal of 60 % | GOST 14236, ISO 527, ASTM D882 |
Zugfestigkeit | 20.0 °C | 70 MPa Show Supplier Material materials with Zugfestigkeit of 70 MPa | GOST 14236, ISO 527, ASTM D882 |
Zugfestigkeit, transversal | 20.0 °C | 140 MPa Show Supplier Material materials with Zugfestigkeit, transversal of 140 MPa | GOST 14236, ISO 527, ASTM D882 |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High quality rotogravure and flexographic solvent based printing; for both side printing or in center of triplex lamination; for lamination with solvent based or solventless polyurethane adhesives; production of flexible packaging with frame cold glue; manufacture of flexible packaging for products with high shelf life; manufacture of lid for trays with food, typically in center of triplex; production of flexible packaging for the bouillon cubes. | |
| Friction | Kinetic coefficient of friction µ= 0.3-0.5 (GOST 27492, ISO 8295, ASTM D 1894). | |
| Other | HOHMLB.M BOPP films comprise: An aluminum layer with increased thickness, a treated modified layer for high adhesion to aluminum, an oriented polypropylene tie layer, a white pearl cavitated core layer of printed polypropylene, an oriented polypropylene tie layer, a white pearl heat sealable, non treated skin layer with standard coefficient of friction. | |
| Processing history | Treatment level: 36 mN/m (ISO 8296, ASTM D 2578). | |