General
Property | Value | Comment |
---|---|---|
Mean Roughness | 0.6 - 1.9 μm Show Supplier Material materials with Mean Roughness of 0.6 - 1.9 μm | wide range of roughness levels according to the EN 10130 standard can be supplied upon request. |
Medidas
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mecánica
Property | Value | Comment |
---|---|---|
Elongación | 34 % Show Supplier Material materials with Elongación of 34 % | min. | for thickness 0.3-0.5 mm | Transverse | A80 |
36 % Show Supplier Material materials with Elongación of 36 % | min. | for thickness 0.5-0.7 mm | Transverse | A80 | |
38 % Show Supplier Material materials with Elongación of 38 % | min. | for thickness 0.7-3 mm | Transverse | A80 | |
Límite elástico | 140 - 250 MPa Show Supplier Material materials with Límite elástico of 140 - 250 MPa | for thickness 0.3-0.5 mm | Transverse |
140 - 230 MPa Show Supplier Material materials with Límite elástico of 140 - 230 MPa | for thickness 0.5-0.7 mm | Transverse | |
140 - 210 MPa Show Supplier Material materials with Límite elástico of 140 - 210 MPa | for thickness 0.7-3 mm | Transverse | |
Plastic strain ratio | 1.6 [-] Show Supplier Material materials with Plastic strain ratio of 1.6 [-] | min. | 90ᵒ Transverse | for thickness 2-3 mm |
1.8 [-] Show Supplier Material materials with Plastic strain ratio of 1.8 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm | |
Resistencia a la fatiga | 267 MPa Show Supplier Material materials with Resistencia a la fatiga of 267 MPa | at 5*10⁶ cycles | for thickness 2 mm |
Resistencia a la tracción | 270 - 350 MPa Show Supplier Material materials with Resistencia a la tracción of 270 - 350 MPa | for thickness 0.3-3 mm | Transverse |
Strain hardening exponent | 0.19 [-] Show Supplier Material materials with Strain hardening exponent of 0.19 [-] | min. | 90ᵒ Transverse | for thickness 0.5-3 mm |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminio | 0.02 % Show Supplier Material materials with Aluminio of 0.02 % | max. |
Azufre | 0.025 % Show Supplier Material materials with Azufre of 0.025 % | max. |
Carbono | 0.08 % Show Supplier Material materials with Carbono of 0.08 % | max. |
Fósforo | 0.025 % Show Supplier Material materials with Fósforo of 0.025 % | max. |
Manganeso | 0.4 % Show Supplier Material materials with Manganeso of 0.4 % | max. |
Silicona | 0.03 % Show Supplier Material materials with Silicona of 0.03 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Used for bending and deep drawing forming processes for applications where strength, rigidity and ductility are required. Typical applications are to be found in the automotive industry, the domestic appliance sector, metal furniture, drums, radiators, fans, small welded tubes and small profiles. Uncoated cold rolled steels for cold forming are suitable for food contact, under certain conditions laid down in the Regulation (EC) No. 1935/2004 and the French standard NF A 36-714. Please contact us for further information on this subject. | |
Coating | Galvanisation: Class 1 | |
Surface Finish | This grade is available in: | |
Surface condition | Surface cleanliness If improved surface cleanliness is required, ArcelorMittal also offers with compulsory use of hydrogen annealing. | |
Welding | Weldability is guaranteed when using the usual processes. Please specify which process you intend to use when ordering. | |
Workability | ArcelorMittal steel grade DC04 for cold forming have excellent drawability in all types of forming processes. They can be used to manufacture complex, multifunctional parts, and allow significant savings. Forming limit curves can be used to define the maximum strains not to be exceeded when forming steel by various methods, so as to avoid the risk of incipient necking. These curves are available on request. |