Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mecánica
Property | Value | Comment |
---|---|---|
Elongación | 40 % Show Supplier Material materials with Elongación of 40 % | min. | for thickness 0.5-3 mm | Transverse | A80 |
Límite elástico | 90 - 160 MPa Show Supplier Material materials with Límite elástico of 90 - 160 MPa | for thickness 0.5-3 mm | Transverse |
Plastic strain ratio | 1.5 [-] Show Supplier Material materials with Plastic strain ratio of 1.5 [-] | min. | 90ᵒ Transverse | for thickness 2-3 mm |
1.7 [-] Show Supplier Material materials with Plastic strain ratio of 1.7 [-] | min. | 90ᵒ Transverse | for thickness 0.5-2 mm | |
Resistencia a la tracción | 270 - 350 MPa Show Supplier Material materials with Resistencia a la tracción of 270 - 350 MPa | for thickness 0.5-3 mm | Transverse |
Strain hardening exponent | 0.19 [-] Show Supplier Material materials with Strain hardening exponent of 0.19 [-] | min. | 90ᵒ Transverse | for thickness 0.5-3 mm |
Chemical properties
Property | Value | Comment |
---|---|---|
Azufre | 0.05 % Show Supplier Material materials with Azufre of 0.05 % | max. |
Carbono | 0.02 % Show Supplier Material materials with Carbono of 0.02 % | max. |
Fósforo | 0.03 % Show Supplier Material materials with Fósforo of 0.03 % | max. |
Manganeso | 0.5 % Show Supplier Material materials with Manganeso of 0.5 % | max. |
Titanio | 0.2 % Show Supplier Material materials with Titanio of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | This steel has many applications: | |
Coating | Enamelling Surface preparation: Application of the enamel and firing: Finally, firing is performed at a temperature of about 830°C. | |
Joining | It can be welded without any difficulty, whatever the welding process may be. Other joining processes (clinching, crimping) may also be used. | |
Processing methods | DC07EK AM FCE, interstitial free steel (IFS) with low carbon content and excellent rheological and mechanical properties, can be used for forming very complex parts. |