Propiedades
Medidas
| Property | Value |
|---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mecánica
| Property | Value | Comment |
|---|---|---|
Elongación | 20 % Show Supplier Material materials with Elongación of 20 % | min. |
Límite elástico | 280 - 380 MPa Show Supplier Material materials with Límite elástico of 280 - 380 MPa | As delivered | The guaranteed minimum yield strength after 5% deformation and enamel firing is 300 MPa |
Resistencia a la tracción | 360 - 480 MPa Show Supplier Material materials with Resistencia a la tracción of 360 - 480 MPa | As delivered |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Azufre | 0.025 % Show Supplier Material materials with Azufre of 0.025 % | max. |
Carbono | 0.075 % Show Supplier Material materials with Carbono of 0.075 % | max. |
Fósforo | 0.075 % Show Supplier Material materials with Fósforo of 0.075 % | max. |
Manganeso | 0.5 % Show Supplier Material materials with Manganeso of 0.5 % | max. |
Nitrógeno | 0.006 % Show Supplier Material materials with Nitrógeno of 0.006 % | max. |
Silicona | 0.5 % Show Supplier Material materials with Silicona of 0.5 % | max. |
Technological properties
| Property | ||
|---|---|---|
| Application areas | HC300EK grade is particularly suitable for the manufacture of water heater tanks. It can also be used for flat parts for household items (dripping pans, baking trays) and shower trays or for manufacturing architectural panels for building interiors or exteriors. | |
| Chemical composition | The manufacturing conditions guarantee very good resistance to “fish scale” defects (TH > 100 in accordance with EN 10209). | |
| Coating | Enamelling Surface treatment: The parts must be degreased before enamelling. When enamel containing a low level of adhesion oxides is used (e.g. water heater tank using Ni-free enamel), sand blasting or pickling may be necessary. Enamel application and firing: HC300EK grade is compatible with all the common enamelling processes: wet spraying, electrostatic liquid or powder enamelling. Both ground and conventional enamelling processes are feasible. Where wet application is used, it is imperative to dry the enamel layer before firing. Enamel firing is carried out at 830°C. | |
| Joining | HC300EK grade can easily be welded, whatever the welding process may be. Other joining processes (clinching, crimping) may also be used. | |
| Processing methods | HC300EK grade can be formed by bending, profiling or light drawing. | |