General
Property | Value | Comment |
---|---|---|
Densidad | 7.85 g/cm³ Show Supplier Material materials with Densidad of 7.85 g/cm³ | for thickness 0.5 mm |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 120 - 150 [-] Show Supplier Material materials with Dureza Vickers of 120 - 150 [-] | for thickness 0.5 mm |
Elongación | 27 - 37 % Show Supplier Material materials with Elongación of 27 - 37 % | for thickness 0.5 mm | Transverse | A80 |
Límite elástico | 290 - 350 MPa Show Supplier Material materials with Límite elástico of 290 - 350 MPa | for thickness 0.5 mm | Transverse |
Number of bends | 10 [-] Show Supplier Material materials with Number of bends of 10 [-] | min. for thickness 0.5 mm | Guaranteed |
Resistencia a la tracción | 420 - 460 MPa Show Supplier Material materials with Resistencia a la tracción of 420 - 460 MPa | for thickness 0.5 mm | Transverse |
Yield to strength ratio | 0.69 - 0.74 [-] Show Supplier Material materials with Yield to strength ratio of 0.69 - 0.74 [-] | for thickness 0.5 mm |
Magnético
Property | Value | Frequency | Comment |
---|---|---|---|
Anisotropy of loss | 8 % Show Supplier Material materials with Anisotropy of loss of 8 % | (+/-) for thickness 0.5 mm | Guaranteed | |
Polarización garantizada | 1.62 [-] Show Supplier Material materials with Polarización garantizada of 1.62 [-] | min. | for thickness 0.5 mm | at 2500 A/m | |
1.72 [-] Show Supplier Material materials with Polarización garantizada of 1.72 [-] | min. | for thickness 0.5 mm | at 5000 A/m | ||
1.81 [-] Show Supplier Material materials with Polarización garantizada of 1.81 [-] | min. | for thickness 0.5 mm | at 10000 A/m | ||
Pérdida en el núcleo garantizada | 9.4 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 9.4 W/kg | 50Hz | max. for thickness 0.5 mm | at 1.5 T |
Pérdida en el núcleo normal | 4.2 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 4.2 W/kg | 50Hz | max. for thickness 0.5 mm | at 1 T |
11.84 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 11.84 W/kg | 60Hz | max. for thickness 0.5 mm | at 1.5 T | |
Stacking factor | 0.96 mm Show Supplier Material materials with Stacking factor of 0.96 mm | min. | for thickness 0.5 mm | Guaranteed |
Technological properties
Property | ||
---|---|---|
Application areas | The fully processed steel is designed for the manufacture of magnetic circuits for motors, transformers and other electrical equipment. The principal applications are in the electrical engineering, domestic appliance, automotive and building industries. Low loss fully processed steels are also suitable for shielding applications at low frequencies (e.g. housings around electrical systems). | |
Coating | This standard grade is available non-insulated or varnished with any of the coating types described in the following link https://industry.arcelormittal.com/catalogue/D28/EN . | |
Other | Recommendations for use The are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |