Propiedades
General
| Property | Value | Comment |
|---|---|---|
Densidad | 7.75 g/cm³ Show Supplier Material materials with Densidad of 7.75 g/cm³ | for thickness 0.50 mm |
Mecánica
| Property | Value | Comment |
|---|---|---|
Dureza Vickers | 135 - 165 [-] Show Supplier Material materials with Dureza Vickers of 135 - 165 [-] | for thickness 0.50 mm |
Elongación | 27 - 37 % Show Supplier Material materials with Elongación of 27 - 37 % | for thickness 0.50 mm | Transverse | A80 |
Límite elástico | 250 - 350 MPa Show Supplier Material materials with Límite elástico of 250 - 350 MPa | for thickness 0.50 mm | Transverse |
Number of bends | 3 [-] Show Supplier Material materials with Number of bends of 3 [-] | min. for thickness 0.50 mm | Guaranteed |
Resistencia a la tracción | 400 - 450 MPa Show Supplier Material materials with Resistencia a la tracción of 400 - 450 MPa | for thickness 0.50 mm | Transverse |
Yield to strength ratio | 0.61 - 0.66 [-] Show Supplier Material materials with Yield to strength ratio of 0.61 - 0.66 [-] | for thickness 0.50 mm |
Magnético
| Property | Value | Frequency | Comment |
|---|---|---|---|
Anisotropy of loss | 14 % Show Supplier Material materials with Anisotropy of loss of 14 % | (+/-) for thickness 0.50 mm | Guaranteed | |
Polarización garantizada | 1.62 [-] Show Supplier Material materials with Polarización garantizada of 1.62 [-] | min. | for thickness 0.50 mm | at 2500 A/m | |
1.72 [-] Show Supplier Material materials with Polarización garantizada of 1.72 [-] | min. | for thickness 0.50 mm | Indicative | ||
1.83 [-] Show Supplier Material materials with Polarización garantizada of 1.83 [-] | min. | for thickness 0.50 mm | at 10000 A/m | ||
Pérdida en el núcleo garantizada | 3.3 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 3.3 W/kg | 50Hz | max. for thickness 0.50 mm | at 1.5 T |
Pérdida en el núcleo normal | 1.45 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 1.45 W/kg | 50Hz | max. for thickness 0.50 mm | at 1 T |
4.2 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 4.2 W/kg | 60Hz | max. for thickness 0.50 mm | at 1.5 T | |
Stacking factor | 0.96 mm Show Supplier Material materials with Stacking factor of 0.96 mm | min. | for thickness 0.50 mm | Guaranteed |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High permeability is particularly useful for applications such as ballasts and motors, because it makes it possible to build machines that meet the most stringent environmental regulations. High thermal conductivity is a significant advantage for large machines. | |
| Coating | This high permeability grade is available non-insulated or varnished. | |
| Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. | |