General
Property | Value | Comment |
---|---|---|
Densidad | 7.75 g/cm³ Show Supplier Material materials with Densidad of 7.75 g/cm³ | for thickness 0.50 mm |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 140 - 170 [-] Show Supplier Material materials with Dureza Vickers of 140 - 170 [-] | for thickness 0.50 mm |
Elongación | 27 - 37 % Show Supplier Material materials with Elongación of 27 - 37 % | for thickness 0.50 mm | Transverse | A80 |
Límite elástico | 270 - 320 MPa Show Supplier Material materials with Límite elástico of 270 - 320 MPa | for thickness 0.50 mm | Transverse |
Number of bends | 10 [-] Show Supplier Material materials with Number of bends of 10 [-] | min. for thickness 0.50 mm | Guaranteed |
Resistencia a la tracción | 430 - 480 MPa Show Supplier Material materials with Resistencia a la tracción of 430 - 480 MPa | for thickness 0.50 mm | Transverse |
Yield to strength ratio | 0.63 - 0.68 [-] Show Supplier Material materials with Yield to strength ratio of 0.63 - 0.68 [-] | for thickness 0.50 mm |
Magnético
Property | Value | Frequency | Comment |
---|---|---|---|
Anisotropy of loss | 10 % Show Supplier Material materials with Anisotropy of loss of 10 % | (+/-) for thickness 0.50 mm | Guaranteed | |
Polarización garantizada | 1.62 [-] Show Supplier Material materials with Polarización garantizada of 1.62 [-] | min. | for thickness 0.50 mm | at 2500 A/m | |
1.72 [-] Show Supplier Material materials with Polarización garantizada of 1.72 [-] | min. | for thickness 0.50 mm | Indicative | ||
1.83 [-] Show Supplier Material materials with Polarización garantizada of 1.83 [-] | min. | for thickness 0.50 mm | at 10000 A/m | ||
Pérdida en el núcleo garantizada | 4.7 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 4.7 W/kg | 50Hz | max. for thickness 0.50 mm | at 1.5 T |
Pérdida en el núcleo normal | 2 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 2 W/kg | 50Hz | max. for thickness 0.50 mm | at 1 T |
5.9 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 5.9 W/kg | 60Hz | max. for thickness 0.50 mm | at 1.5 T | |
Stacking factor | 0.96 mm Show Supplier Material materials with Stacking factor of 0.96 mm | min. | for thickness 0.50 mm | Guaranteed |
Technological properties
Property | ||
---|---|---|
Application areas | High permeability is particularly useful for applications such as ballasts and motors, because it makes it possible to build machines that meet the most stringent environmental regulations. High thermal conductivity is a significant advantage for large machines. | |
Coating | This high permeability grade is available non-insulated or varnished. | |
Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |