Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.6 g/cm³ Show Supplier Material materials with Densidad of 7.6 g/cm³ |
Mecánica
| Property | Value | Comment |
|---|---|---|
Dureza Vickers | 205 - 235 [-] Show Supplier Material materials with Dureza Vickers of 205 - 235 [-] | |
Elongación | 12 - 22 % Show Supplier Material materials with Elongación of 12 - 22 % | A80 |
Límite elástico | 395 - 435 MPa Show Supplier Material materials with Límite elástico of 395 - 435 MPa | |
Number of bends | 2 [-] Show Supplier Material materials with Number of bends of 2 [-] | min. Guaranteed |
Resistencia a la tracción | 505 - 545 MPa Show Supplier Material materials with Resistencia a la tracción of 505 - 545 MPa | |
Yield to strength ratio | 0.78 - 0.83 [-] Show Supplier Material materials with Yield to strength ratio of 0.78 - 0.83 [-] |
Magnético
| Property | Value | Frequency | Comment |
|---|---|---|---|
Polarización garantizada | 1.48 [-] Show Supplier Material materials with Polarización garantizada of 1.48 [-] | min. | at 2500 A/m | |
1.59 [-] Show Supplier Material materials with Polarización garantizada of 1.59 [-] | min. | at 5000 A/m | ||
1.69 [-] Show Supplier Material materials with Polarización garantizada of 1.69 [-] | min. | at 10000 A/m | ||
Pérdida en el núcleo garantizada | 15 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 15 W/kg | 400Hz | max. at 1 T |
Pérdida en el núcleo normal | 32 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 32 W/kg | 700Hz | at 1 T |
38 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 38 W/kg | 400Hz | max. at 1.5 T | |
Stacking factor | 0.93 mm Show Supplier Material materials with Stacking factor of 0.93 mm | min. | Guaranteed |
Technological properties
| Property | ||
|---|---|---|
| Application areas | This grade is designed for high speed rotating machines (100 to 5000 Hz). It allows minimisation of losses due to higher harmonics and clearly increases machine efficiency in the case of non-sinusoidal power supply. This thin, fully processed grade is also used when weight and volume reduction are of major importance, such as in medical or aviation applications. | |
| Coating | This high frequency grade is available non-insulated or varnished with a C5-type coating. | |
| Other | The above properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. | |