General
Property | Value |
---|---|
Densidad | 7.65 g/cm³ Show Supplier Material materials with Densidad of 7.65 g/cm³ |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 185 - 235 [-] Show Supplier Material materials with Dureza Vickers of 185 - 235 [-] | for thickness 0.65 mm |
Elongación | 10 - 21 % Show Supplier Material materials with Elongación of 10 - 21 % | for thickness 0.65 mm | Transverse | A80 |
Límite elástico | 505 - 565 MPa Show Supplier Material materials with Límite elástico of 505 - 565 MPa | for thickness 0.65 mm | Transverse |
Resistencia a la tracción | 560 - 610 MPa Show Supplier Material materials with Resistencia a la tracción of 560 - 610 MPa | for thickness 0.65 mm | Transverse |
Magnético
Property | Value | Frequency | Comment |
---|---|---|---|
Polarización garantizada | 1.54 [-] Show Supplier Material materials with Polarización garantizada of 1.54 [-] | min. | for thickness 0.65 mm | at 2500 A/m | |
1.62 [-] Show Supplier Material materials with Polarización garantizada of 1.62 [-] | min. | for thickness 0.65 mm | at 5000 A/m | ||
1.72 [-] Show Supplier Material materials with Polarización garantizada of 1.72 [-] | min. | for thickness 0.65 mm | at 10000 A/m | ||
Pérdida en el núcleo garantizada | 3.9 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 3.9 W/kg | 50Hz | max. for thickness 0.65 mm | at 1 T |
Pérdida en el núcleo normal | 1.62 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 1.62 W/kg | 50Hz | max. for thickness 0.65 mm | at 1 T |
5.07 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 5.07 W/kg | 60Hz | max. for thickness 0.65 mm | at 1.5 T |
Technological properties
Property | ||
---|---|---|
Application areas | Non-alloyed semi-processed electrical steels are designed for small industrial motors, fans and domestic appliances such as washing machine motors, microwave oven transformers and refrigerator compressors. Alloyed semi-processed electrical steels are designed for similar higher efficiency versions of these applications, as they have lower losses whilst the permeability remains at a good level. | |
Coating | This semi-processed grade is available non-insulated. The final process step in the decarburising annealing treatment carried out by the client provides a suitable atmosphere and thermal conditions for blueing: the formation of an oxide film, which creates the required surface insulation layer. | |
Other | The punching process needs to be carried out with an appropriate lubricant, which must be selected carefully, especially in the case of the alloyed semi-processed grades. |