General
Property | Value |
---|---|
Densidad | 7.85 g/cm³ Show Supplier Material materials with Densidad of 7.85 g/cm³ |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 130 - 180 [-] Show Supplier Material materials with Dureza Vickers of 130 - 180 [-] | for thickness 0.65 mm |
Elongación | 30 % Show Supplier Material materials with Elongación of 30 % | min. | for thickness 0.65 mm | Transverse | A80 |
Límite elástico | 350 - 490 MPa Show Supplier Material materials with Límite elástico of 350 - 490 MPa | for thickness 0.65 mm | Transverse |
Resistencia a la tracción | 380 - 500 MPa Show Supplier Material materials with Resistencia a la tracción of 380 - 500 MPa | for thickness 0.65 mm | Transverse |
Magnético
Property | Value | Frequency | Comment | ||
---|---|---|---|---|---|
Polarización garantizada | 1.61 [-] Show Supplier Material materials with Polarización garantizada of 1.61 [-] | min. | for thickness 0.65 mm | at 2500 A/m | |||
1.68 [-] Show Supplier Material materials with Polarización garantizada of 1.68 [-] | min. | for thickness 0.65 mm | at 5000 A/m | ||||
1.79 [-] Show Supplier Material materials with Polarización garantizada of 1.79 [-] | min. | for thickness 0.65 mm | at 10000 A/m | ||||
Pérdida en el núcleo garantizada | 6 W/kg Show Supplier Material materials with Pérdida en el núcleo garantizada of 6 W/kg | 50Hz | max. for thickness 0.65 mm | at 1.5 T | ||
Pérdida en el núcleo normal | 2.4 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 2.4 W/kg | 50Hz | max. for thickness 0.65 mm | at 1 T | ||
7.6 W/kg Show Supplier Material materials with Pérdida en el núcleo normal of 7.6 W/kg | 60Hz | max. for thickness 0.65 mm | at 1.5 T | |||
Magnetic properties | The very high permeability grades (XP) offer excellent performance at 45°, with J2500 up to 1.79 T. Deviating from the standard Epstein test, we guarantee for these grades the average values measured in all directions of the sheet plane. These values are representative of the real material behaviour in a rotating machine. The magnetic properties given for the high permeability grades (P) refer to the standard Epstein test (mixture of L and T direction). |
Technological properties
Property | ||
---|---|---|
Application areas | This semi-processed high permeability grade is designed for motors, generators, transformers, converters and ballasts where higher efficiency is required. | |
Coating | As with the standard grades, the high permeability grade is available non-insulated. However, this high permeability grade can be supplied with an organic or inorganic-organic coating to meet higher insulating requirements. | |
Other | It needs no particular machine production process adjustments. |