Property | Value | Comment |
---|---|---|
Dureza Vickers | 140 - 170 [-] Show Supplier Material materials with Dureza Vickers of 140 - 170 [-] | Typical values for thickness 1 mm |
Elongación | 15 % Show Supplier Material materials with Elongación of 15 % | min. | for thickness 1 mm | Transverse | A80 | Guaranteed |
28 - 38 % Show Supplier Material materials with Elongación of 28 - 38 % | for thickness 1 mm | Transverse | A80 | Typical values | |
Límite elástico | 300 MPa Show Supplier Material materials with Límite elástico of 300 MPa | min. | Guaranteed | Transverse |
320 - 360 MPa Show Supplier Material materials with Límite elástico of 320 - 360 MPa | Typical values | Transverse | |
Resistencia a la tracción | 375 MPa Show Supplier Material materials with Resistencia a la tracción of 375 MPa | min. | Guaranteed |
450 - 490 MPa Show Supplier Material materials with Resistencia a la tracción of 450 - 490 MPa | Typical values | |
Yield to strength ratio | 0.7 - 0.75 [-] Show Supplier Material materials with Yield to strength ratio of 0.7 - 0.75 [-] | Typical values |
Magnético
Property | Value | Comment |
---|---|---|
Polarización garantizada | 1.55 [-] Show Supplier Material materials with Polarización garantizada of 1.55 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.82 [-] Show Supplier Material materials with Polarización garantizada of 1.82 [-] | min. | for thickness 1 mm | in DC at 15000 A/m | |
Polarización normal | 1.69 [-] Show Supplier Material materials with Polarización normal of 1.69 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.88 [-] Show Supplier Material materials with Polarización normal of 1.88 [-] | min. | for thickness 1 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |