Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 200 - 230 [-] Show Supplier Material materials with Dureza Vickers of 200 - 230 [-] | Typical values |
Elongación | 10 % Show Supplier Material materials with Elongación of 10 % | min. | for thickness 1 mm | Transverse | A80 | Guaranteed |
20 - 30 % Show Supplier Material materials with Elongación of 20 - 30 % | for thickness 1 mm | Transverse | A80 | Typical values | |
Límite elástico | 450 MPa Show Supplier Material materials with Límite elástico of 450 MPa | min. | Guaranteed | Transverse |
480 - 520 MPa Show Supplier Material materials with Límite elástico of 480 - 520 MPa | Typical values | Transverse | |
Resistencia a la tracción | 500 MPa Show Supplier Material materials with Resistencia a la tracción of 500 MPa | min. | Guaranteed |
580 - 620 MPa Show Supplier Material materials with Resistencia a la tracción of 580 - 620 MPa | Typical values | |
Yield to strength ratio | 0.78 - 0.82 [-] Show Supplier Material materials with Yield to strength ratio of 0.78 - 0.82 [-] | Typical values |
Magnético
Property | Value | Comment |
---|---|---|
Polarización garantizada | 1.5 [-] Show Supplier Material materials with Polarización garantizada of 1.5 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.8 [-] Show Supplier Material materials with Polarización garantizada of 1.8 [-] | min. | for thickness 1 mm | in DC at 15000 A/m | |
Polarización normal | 1.67 [-] Show Supplier Material materials with Polarización normal of 1.67 [-] | min. | for thickness 1 mm | in DC at 5000 A/m |
1.86 [-] Show Supplier Material materials with Polarización normal of 1.86 [-] | min. | for thickness 1 mm | in DC at 15000 A/m |
Technological properties
Property | ||
---|---|---|
Application areas | Cold rolled pole sheet grade is designed for large high-speed machines because of its excellent combination of mechanical strength and magnetic performance. | |
Other | These properties are obtained without heat treatment after stamping. The material as supplied possesses all the required magnetic properties. |