Medidas
Property | Value |
---|---|
Dimensions | Please feel free to check the figure on the right side of the material page for more details. |
Mecánica
Property | Value | Comment |
---|---|---|
Elongación | 11 % Show Supplier Material materials with Elongación of 11 % | min. | for thickness 0.2-0.35 mm | A80 |
14 % Show Supplier Material materials with Elongación of 14 % | min. | for thickness 0.35-5 mm | A80 | |
16 % Show Supplier Material materials with Elongación of 16 % | min. | for thickness 0.5-7 mm | A80 | |
18 % Show Supplier Material materials with Elongación of 18 % | min. | for thickness 0.7-3 mm | A80 | |
Límite elástico | 280 MPa Show Supplier Material materials with Límite elástico of 280 MPa | min. | for thickness 0.2-3 mm |
Resistencia a la tracción | 360 MPa Show Supplier Material materials with Resistencia a la tracción of 360 MPa | min. | for thickness 0.2-3 mm |
Chemical properties
Property | Value | Comment |
---|---|---|
Azufre | 0.045 % Show Supplier Material materials with Azufre of 0.045 % | max. |
Carbono | 0.2 % Show Supplier Material materials with Carbono of 0.2 % | max. |
Fósforo | 0.1 % Show Supplier Material materials with Fósforo of 0.1 % | max. |
Manganeso | 1.7 % Show Supplier Material materials with Manganeso of 1.7 % | max. |
Silicona | 0.6 % Show Supplier Material materials with Silicona of 0.6 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | Galfan is used in numerous industrial applications, such as: | |
Coating | ||
Other | Storage Galvanised strips are usually supplied passivated or oiled to temporarily limit any risk of white rust formation. During transport and storage, all necessary precautions must be taken to keep the material dry and to prevent the formation of condensation. Improved protection can be achieved by the application of an Easyfilm® thin organic coating (please see data sheet E80 for the specific properties of Easyfilm®). Forming and joining The forming and joining techniques currently used for uncoated steel are also suitable for galvanised steel. It is essential to select a coating thickness that is compatible with the forming and joining processes envisaged, without compromising the desired degree of corrosion protection. Painting Hot dip galvanised steels can be painted after degreasing and surface treatment when supplied oiled. If an Easyfilm® thin organic coating has been applied, they can be painted directly, without any prior surface treatment. However, the paint must be compatible with the Easyfilm® resin. | |
Welding | In electrical resistance welding, the welding current must be suitably regulated and regularly adjusted. Electrode life can be extended by regularly stepping up the welding current and periodically dressing (machining) the electrodes. |