General
Property | Temperature | Value | |
---|---|---|---|
Densidad | 23.0 °C | 14.45 g/cm³ Show Supplier Material materials with Densidad of 14.45 g/cm³ | |
Aglutinante | Cobalt binder | ||
Estructura de grano | Submicron grain size |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Rockwell A | 23.0 °C | 92.3 [-] Show Supplier Material materials with Dureza Rockwell A of 92.3 [-] |
Dureza Vickers | 23.0 °C | 1680 [-] Show Supplier Material materials with Dureza Vickers of 1680 [-] |
Módulo elástico | 23.0 °C | 580 GPa Show Supplier Material materials with Módulo elástico of 580 GPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 9.4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 9.4 MPa·√m |
Resistencia a la compresión | 23.0 °C | 6600 MPa Show Supplier Material materials with Resistencia a la compresión of 6600 MPa |
Resistencia a la tracción transversal | 23.0 °C | 3700 MPa Show Supplier Material materials with Resistencia a la tracción transversal of 3700 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.5E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.5E-6 1/K |
Conductividad térmica | 23.0 °C | 85 W/(m·K) Show Supplier Material materials with Conductividad térmica of 85 W/(m·K) |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Cobalto | 10 % Show Supplier Material materials with Cobalto of 10 % | as binder | |
Wolframio | WC balance |
Technological properties
Property |
---|