General
Property | Temperature | Value | |
---|---|---|---|
Densidad | 23.0 °C | 12.2 g/cm³ Show Supplier Material materials with Densidad of 12.2 g/cm³ | |
Aglutinante | Cobalt binder | ||
Estructura de grano | Fine grain size |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Rockwell A | 23.0 °C | 91.6 [-] Show Supplier Material materials with Dureza Rockwell A of 91.6 [-] |
Dureza Vickers | 23.0 °C | 1570 [-] Show Supplier Material materials with Dureza Vickers of 1570 [-] |
Módulo elástico | 23.0 °C | 505 GPa Show Supplier Material materials with Módulo elástico of 505 GPa |
Plane-Strain Fracture Toughnes | 23.0 °C | 10.8 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 10.8 MPa·√m |
Resistencia a la compresión | 23.0 °C | 5100 MPa Show Supplier Material materials with Resistencia a la compresión of 5100 MPa |
Resistencia a la tracción transversal | 23.0 °C | 1700 MPa Show Supplier Material materials with Resistencia a la tracción transversal of 1700 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6E-6 1/K |
Conductividad térmica | 23.0 °C | 50 W/(m·K) Show Supplier Material materials with Conductividad térmica of 50 W/(m·K) |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Cobalto | 9.5 % Show Supplier Material materials with Cobalto of 9.5 % | as binder | |
Wolframio | WC balance |
Technological properties
Property |
---|