General
Property | Temperature | Value | |
---|---|---|---|
Densidad | 23.0 °C | 14.55 g/cm³ Show Supplier Material materials with Densidad of 14.55 g/cm³ | |
Estructura de grano | Ultrafine (0,2µm - 0,5µm) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.21 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.21 [-] | |
Dureza Rockwell A | 23.0 °C | 93.7 [-] Show Supplier Material materials with Dureza Rockwell A of 93.7 [-] | |
Dureza Vickers 10 | 23.0 °C | 1970 [-] Show Supplier Material materials with Dureza Vickers 10 of 1970 [-] | EN ISO 6507-1 |
Dureza Vickers 30 | 23.0 °C | 1930 [-] Show Supplier Material materials with Dureza Vickers 30 of 1930 [-] | EN ISO 6507-1 |
Módulo elástico | 23.0 °C | 596 GPa Show Supplier Material materials with Módulo elástico of 596 GPa | |
Plane-Strain Fracture Toughnes | 23.0 °C | 9.2 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 9.2 MPa·√m | ISO 28079 |
Resistencia a la tracción transversal | 23.0 °C | 4400 MPa Show Supplier Material materials with Resistencia a la tracción transversal of 4400 MPa | DIN EN ISO 7438 |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.02E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.02E-6 1/K |
Chemical properties
Technological properties
Property |
---|