Propiedades
General
| Property | Value | Comment |
|---|---|---|
Absorción de agua | 0.1 % Show Supplier Material materials with Absorción de agua of 0.1 % | |
Densidad | 3.73 g/cm³ Show Supplier Material materials with Densidad of 3.73 g/cm³ | |
Rugosidad superficial | 0.8 μm Show Supplier Material materials with Rugosidad superficial of 0.8 μm | as fired surface |
Mecánica
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Resistencia a la flexión | 300 MPa Show Supplier Material materials with Resistencia a la flexión of 300 MPa | DR sigma 0 | 0.63-1.00 mm thickness | rings 6 / 12 mm |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 20 °C | 0.7 J/(kg·K) Show Supplier Material materials with Calor específico of 0.7 J/(kg·K) | |
100 °C | 0.9 J/(kg·K) Show Supplier Material materials with Calor específico of 0.9 J/(kg·K) | ||
Conductividad térmica | 20 °C | 22 W/(m·K) Show Supplier Material materials with Conductividad térmica of 22 W/(m·K) | Xe-flash | sample 16*16mm² | material specific thickness ≤ 3.5mm |
Eléctrico
| Property | Temperature | Value | Frequency | Comment |
|---|---|---|---|---|
Constante dieléctrica | 8.3 - 11.3 [-] Show Supplier Material materials with Constante dieléctrica of 8.3 - 11.3 [-] | 1 GHz, 10 MHz, 100 MHz | 2mm thickness | Ra ≤ 0.4μm | |
Factor de disipación | 0.01 [-] Show Supplier Material materials with Factor de disipación of 0.01 [-] | 1 GHz, 10 MHz, 100 MHz | max. | 2mm thickness | Ra ≤ 0.4μm | |
Resistividad eléctrica | 20 °C | 1e+11 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1e+11 Ω·m | ||
200 °C | 1e+09 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1e+09 Ω·m | |||
400 °C | 1e+07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 1e+07 Ω·m | |||
600 °C | 100000 Ω·m Show Supplier Material materials with Resistividad eléctrica of 100000 Ω·m |
Technological properties
| Property | ||
|---|---|---|
| Application areas | CeramTec uses Rubalit® alumina ceramics for CeramCore cores for metal-oxide, carbon-film, metal-layered, thin-film and wire-wound resistors. The fine structures of Rubalit® 600, 702 und 708 play a vital role in delivering very high and consistent surface quality. Using Rubalit® 600, 702 und 708 as core materials help create resistors with a lower noise factor and more stable resistance, increases resistance against electrical shock loads and improves reliability in laser trimming. This makes it possible to achieve higher integration density while simultaneously ensuring higher power density. CeramTec boasts decades of manufacturing experience, enabling the company to produce ceramic parts for passive components with tight dimensional tolerances while delivering very high surface quality even for large-scale production with quantities ranging in the billions. | |
| Chemical composition | The material main component is Al₂O₃ with 95.8% content. Residue mainly consists of MgO, SiO2 and CaO and traces of other elements. | |