Property | Value | Testing Standard |
---|---|---|
Densidad | 1.07 g/cm³ Show Supplier Material materials with Densidad of 1.07 g/cm³ | ISO 1183-1 |
Mecánica
Property | Temperature | Value | Testing Standard | Comment |
---|---|---|---|---|
Elongación | 53 % Show Supplier Material materials with Elongación of 53 % | ISO 527-1/2 | 50 mm/min | |
Elongation at yield | 4.1 % Show Supplier Material materials with Elongation at yield of 4.1 % | ISO 527-1/2 | 50 mm/min | |
Hardness, Ball Indentation | 90 MPa Show Supplier Material materials with Hardness, Ball Indentation of 90 MPa | ISO 2039-1 | ||
Límite elástico | 42 MPa Show Supplier Material materials with Límite elástico of 42 MPa | ISO 527-1/2 | 50 mm/min | |
Módulo de flexión | 2 GPa Show Supplier Material materials with Módulo de flexión of 2 GPa | ISO 527-1/2 | 2 mm/min | |
Módulo elástico | 2 GPa Show Supplier Material materials with Módulo elástico of 2 GPa | ISO 527-1/2 | 1 mm/min | |
Resistencia a la flexión | 68 MPa Show Supplier Material materials with Resistencia a la flexión of 68 MPa | ISO 178 | 2 mm/min | |
Resistencia al choque, ensayo Charpy entallado | -30 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 40 kJ/m² | ISO 179-1eA | |
23 °C | 53 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 53 kJ/m² | ISO 179-1eA | ||
Resistencia al choque, ensayo Izod entallado | -30 °C | 41 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 41 kJ/m² | ISO 180-1A | |
23 °C | 58 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 58 kJ/m² | ISO 180-1A |
Aplicaciones térmicas
Property | Value | Testing Standard | Pressure | Comment | |||
---|---|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 8.9e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.9e-05 1/K | ISO 11359-1/2 | 23 to 55°C | ||||
Temperatura de flexión bajo carga | 101 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 101 °C | ISO 75-1/2 | 1.8 MPa | ||||
113 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 113 °C | ISO 75-1/2 | 0.45 MPa | |||||
Temperatura de reblandecimiento Vicat | 113 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 113 °C | ISO 306 | B50 | 50°C/h | ||||
115 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 115 °C | ISO 306 | B120 | 120°C/h | |||||
Inflamabilidad | At thickness 1.6 mm UL 94: HB. Burning rate US-FMVSS (150x110x2 mm): 40 mm/min | max. | according to ISO 3795 |
Rheological Properties
Property | Value | Testing Standard | Comment |
---|---|---|---|
Contracción | 0.65 - 0.75 % Show Supplier Material materials with Contracción of 0.65 - 0.75 % | ISO 2577 | 60x60x2 |
0.65 - 0.75 % Show Supplier Material materials with Contracción of 0.65 - 0.75 % | ISO 2577 | 60x60x2, Transverse | |
Velocidad de flujo del volumen derretido | 14 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 14 cm³/10min | ISO 1133 | 260°C/5Kg |
Technological properties
Property | ||
---|---|---|
Certifications | UL Certificate | |
Chemical composition | Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide). | |
Color | White to slightly yellowish. | |
Handling recommendations | Please see the Material Safety Data Sheet for relevant health & safety information. | |
Other | Control measurements in other places may issue different results due to influences of machinery, equipment, test method or storage conditions. | |
Processing methods | Injection molding-melt temperature: 240 ºC according to ISO 294 Injection molding-mold temperature: 70 ºC according to ISO 294 Injection molding-injection velocity: 240 mm/s according to ISO 294 |