General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.28 g/cm³ Show Supplier Material materials with Densidad of 1.28 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Módulo de flexión | 23.0 °C | 6.9 GPa Show Supplier Material materials with Módulo de flexión of 6.9 GPa | ISO 178 (2mm/min) | ||
Módulo elástico | 23.0 °C | 7.4 GPa Show Supplier Material materials with Módulo elástico of 7.4 GPa | ISO 527-2 (1mm/min) | ||
Resistencia a la flexión | 23.0 °C | 235 MPa Show Supplier Material materials with Resistencia a la flexión of 235 MPa | ISO 178 (2mm/min) | ||
Resistencia a la tracción | 23.0 °C | 145 MPa Show Supplier Material materials with Resistencia a la tracción of 145 MPa | ISO 527-2 (5mm/min) | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | ||
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 47 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 47 kJ/m² | ISO 179/1eU | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | ||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 42 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 42 kJ/m² | ISO 180/1U | ||
Elongación | ISO 527-2 (5mm/min) |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Contenido de cenizas | 23.0 °C | 20 % Show Supplier Material materials with Contenido de cenizas of 20 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 245 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 245 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 240 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 240 °C | ISO 75-2/A | |||
Temperatura de fusión | 260 °C Show Supplier Material materials with Temperatura de fusión of 260 °C | ISO 3146 | |||
Inflamabilidad | UL94 (0.8mm) HB |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+14 Ω/sq | ASTM D257 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | EN 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Eplamid 66 glass fiber reinforced compounds are used in all sectors of industry, offering a good balance of thermal and mechanical properties. | |
Fillers | 20% Glass Fiber | |
Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. |