Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.35 g/cm³ Show Supplier Material materials with Densidad of 1.35 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 3.5 % Show Supplier Material materials with Elongación of 3.5 % | ISO 527-2 (5mm/min) |
Módulo de flexión | 23.0 °C | 3.6 GPa Show Supplier Material materials with Módulo de flexión of 3.6 GPa | ISO 178 (2mm/min) |
Módulo elástico | 23.0 °C | 4 GPa Show Supplier Material materials with Módulo elástico of 4 GPa | ISO 527-2 (1mm/min) |
Resistencia a la flexión | 23.0 °C | 120 MPa Show Supplier Material materials with Resistencia a la flexión of 120 MPa | ISO 178 (2mm/min) |
Resistencia a la tracción | 23.0 °C | 75 MPa Show Supplier Material materials with Resistencia a la tracción of 75 MPa | ISO 527-2 (5mm/min) |
Resistencia al choque, ensayo Charpy entallado | -30.0 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 45 kJ/m² | ISO 179/1eU |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 40 kJ/m² | ISO 180/1U |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Contenido de cenizas | 23.0 °C | 10 % Show Supplier Material materials with Contenido de cenizas of 10 % | ISO 3451-4 | ||
Heat deflection temperature, 0.45 MPa | 200 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 200 °C | ISO 75-2/B | |||
Heat deflection temperature, 1.80 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 185 °C | ISO 75-2/A | |||
Temperatura de fusión | 225 °C Show Supplier Material materials with Temperatura de fusión of 225 °C | ISO 3146 | |||
Inflamabilidad | UL94 (0.8mm) HB | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+13 Ω/sq | ASTM D257 |
Índice de seguimiento comparativo | 23.0 °C | 400 V Show Supplier Material materials with Índice de seguimiento comparativo of 400 V | EN 60112 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | EPIMIX PBT ımpact modified and glass fiber reinforced compounds are used in all sectors of industry, offering a good impact strength for mechanical properties and ensures an outstanding performance even at low temperatures (up to -40°C). | |
| Fillers | 10% Glass Fiber | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |