Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.14 g/cm³ Show Supplier Material materials with Densidad of 1.14 g/cm³ | ISO 1183 |
Water content | 23.0 °C | 0.1 % Show Supplier Material materials with Water content of 0.1 % | ISO 15512 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 40 % Show Supplier Material materials with Elongación of 40 % | ISO 527-2 (5mm/min) | ||
Módulo de flexión | 23.0 °C | 2.8 GPa Show Supplier Material materials with Módulo de flexión of 2.8 GPa | ISO 178 (2mm/min) | ||
Módulo elástico | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo elástico of 3.1 GPa | ISO 527-2 (1mm/min) | ||
Resistencia a la flexión | 23.0 °C | 105 MPa Show Supplier Material materials with Resistencia a la flexión of 105 MPa | ISO 178 (2mm/min) | ||
Resistencia a la tracción | 23.0 °C | 75 MPa Show Supplier Material materials with Resistencia a la tracción of 75 MPa | ISO 527-2 (50mm/min) | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | Max; ISO 179/1eA | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | Max; ISO 180/1A | ||
Resistencia al choque, ensayo Charpy no entallado | no break at 23°C; ISO 179/1eU | ||||
Resistencia al choque, ensayo Izod no entallado | no break at 23°C; ISO 180/1U | ||||
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-2/B | |
Heat deflection temperature, 1.80 MPa | 55 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-2/A | |
Temperatura de fusión | 222 °C Show Supplier Material materials with Temperatura de fusión of 222 °C | ISO 3146 | |
Inflamabilidad | UL94 (0.8mm) V2, EN 60695-11-10 | ||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1.00E+13 Ω/sq | ASTM D257 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | EN 60112 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1 % Show Supplier Material materials with Contracción of 1 % | ISO 294-4 (3mm) |
Contracción transversal | 23.0 °C | 1.2 % Show Supplier Material materials with Contracción transversal of 1.2 % | ISO 294-4 (3mm) |
Velocidad de flujo del volumen derretido | 160 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 160 cm³/10min | ISO 1133 (275°C/5 kg) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Eplamid 6 offers all primary properties of unreinforced PA6 used in all sectos of industry, super balance of thermal and mechanical properties, especially for thin wall and fast cycle applications. | |
| Other | Laboratory conditions are 23 ±2°C and 45-55 % RH. | |