Propiedades
Mecánica
| Property | Value | Condition | Comment |
|---|---|---|---|
Elongación | 0.7 % Show Supplier Material materials with Elongación of 0.7 % | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Flexural strain | 1.8 % Show Supplier Material materials with Flexural strain of 1.8 % | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Módulo de compresión | 35100.0 MPa Show Supplier Material materials with Módulo de compresión of 35100.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14126 (cured SMC material) |
Módulo de flexión | 39.0 GPa Show Supplier Material materials with Módulo de flexión of 39.0 GPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Módulo elástico | 44.0 GPa Show Supplier Material materials with Módulo elástico of 44.0 GPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Resistencia a la compresión | 323.0 MPa Show Supplier Material materials with Resistencia a la compresión of 323.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14126 (cured SMC material) |
Resistencia a la flexión | 545.0 MPa Show Supplier Material materials with Resistencia a la flexión of 545.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 14125 (cured SMC material) |
Resistencia a la tracción | 263.0 MPa Show Supplier Material materials with Resistencia a la tracción of 263.0 MPa | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | DIN EN ISO 527-4 (cured SMC material) |
Resistencia al choque, ensayo Charpy no entallado | 107.0 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 107.0 kJ/m² | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | EN ISO 179-1 (cured SMC material) |
Rheological Properties
| Property | Value | Condition | Comment |
|---|---|---|---|
Viscosidad | 0.5 Pa·s Show Supplier Material materials with Viscosidad of 0.5 Pa·s | The properties of cured SMC material (68.1 % carbon fiber mass fraction) | (neat resin) |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Semi-structural parts, Supporting structures, structural lightweight applications, Exterior / Interior parts | |
| Fillers | Carbon Fiber | |
| Processing methods | The molding condition for SMC sheets: Molding pressure: 100-200 bar, Molding temperature: 150°C, Molding coverage: 50-80% and Curing time: 3-4 minutes | |