General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.8 g/cm³ Show Supplier Material materials with Densidad of 8.8 g/cm³ |
Medidas
Property | Value |
---|---|
Dimensions | Available size round products (mm): 1-42 |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 23.0 °C | 160 [-] Show Supplier Material materials with Dureza Brinell of 160 [-] |
Dureza Rockwell C | 23.0 °C | 3 [-] Show Supplier Material materials with Dureza Rockwell C of 3 [-] |
Dureza Vickers | 23.0 °C | 160 [-] Show Supplier Material materials with Dureza Vickers of 160 [-] |
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % |
Límite elástico | 23.0 °C | 600 MPa Show Supplier Material materials with Límite elástico of 600 MPa |
Módulo elástico | 23.0 °C | 145 GPa Show Supplier Material materials with Módulo elástico of 145 GPa |
Resistencia a la tracción | 23.0 °C | 550 - 750 MPa Show Supplier Material materials with Resistencia a la tracción of 550 - 750 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.72E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.72E-5 1/K | for 20-200°C |
Conductividad térmica | 23.0 °C | 22 W/(m·K) Show Supplier Material materials with Conductividad térmica of 22 W/(m·K) | for 20-200°C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 2.00E+6 S/m Show Supplier Material materials with Conductividad eléctrica of 2.00E+6 S/m |
Magnético
Property | Temperature | Value |
---|---|---|
Permeabilidad magnética relativa | 23.0 °C | 1 [-] Show Supplier Material materials with Permeabilidad magnética relativa of 1 [-] |
Technological properties
Property | ||
---|---|---|
Application areas | Summary of typical applications: High performance precision mechanical parts, high end screws, optical fibre connectors | |
Corrosion properties | Corrosion resistance rating: 5 out of 5 | |
General machinability | Machinability: 60-80 % | |
Processing history | Condition: H14 |