General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.36 g/cm³ Show Supplier Material materials with Densidad of 8.36 g/cm³ |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Brinell | 23.0 °C | 103 - 170 [-] Show Supplier Material materials with Dureza Brinell of 103 - 170 [-] |
Dureza Rockwell C | 23.0 °C | 0 - 7 [-] Show Supplier Material materials with Dureza Rockwell C of 0 - 7 [-] |
Dureza Vickers | 23.0 °C | 110 - 175 [-] Show Supplier Material materials with Dureza Vickers of 110 - 175 [-] |
Elongación | 23.0 °C | 8 - 18 % Show Supplier Material materials with Elongación of 8 - 18 % |
Límite elástico | 23.0 °C | 220 - 570 MPa Show Supplier Material materials with Límite elástico of 220 - 570 MPa |
Módulo elástico | 23.0 °C | 107 GPa Show Supplier Material materials with Módulo elástico of 107 GPa |
Resistencia a la tracción | 23.0 °C | 410 - 600 MPa Show Supplier Material materials with Resistencia a la tracción of 410 - 600 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.1E-5 1/K | for 20-200°C |
Conductividad térmica | 23.0 °C | 117 W/(m·K) Show Supplier Material materials with Conductividad térmica of 117 W/(m·K) |
Eléctrico
Property | Temperature | Value |
---|---|---|
Conductividad eléctrica | 23.0 °C | 1.50E+7 S/m Show Supplier Material materials with Conductividad eléctrica of 1.50E+7 S/m |
Specific Electrical conductivity | 26 % IACS Show Supplier Material materials with Specific Electrical conductivity of 26 % IACS |