Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 8.36 g/cm³ Show Supplier Material materials with Densidad of 8.36 g/cm³ |
Medidas
| Property | Value | Comment |
|---|---|---|
Diámetro | 0.76 - 12.7 mm Show Supplier Material materials with Diámetro of 0.76 - 12.7 mm | Smaller diameter wire may be produced by wire redrawers. |
Mecánica
| Property | Temperature | Value |
|---|---|---|
Elongación | 23.0 °C | 30 - 75 % Show Supplier Material materials with Elongación of 30 - 75 % |
Límite elástico Rp 0,2 | 23.0 °C | 130 - 210 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 130 - 210 MPa |
Módulo elástico | 23.0 °C | 131 GPa Show Supplier Material materials with Módulo elástico of 131 GPa |
Resistencia a la tracción | 23.0 °C | 410 - 565 MPa Show Supplier Material materials with Resistencia a la tracción of 410 - 565 MPa |
Aplicaciones térmicas
| Property | Temperature | Value |
|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 23.0 °C | 105 W/(m·K) Show Supplier Material materials with Conductividad térmica of 105 W/(m·K) |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Resistividad eléctrica | 23.0 °C | 6.2E-6 - 7.8E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 6.2E-6 - 7.8E-6 Ω·m |
Specific Electrical conductivity | 22 - 28 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 - 28 % IACS |
Chemical properties
| Property | Value | Comment | |
|---|---|---|---|
Berilio | 1.8 - 2 % Show Supplier Material materials with Berilio of 1.8 - 2 % | ||
Cobalto | 0.2 % Show Supplier Material materials with Cobalto of 0.2 % | min. Nickel + Cobalt | |
Cobre | Balance | ||
Hierro | 0.6 % Show Supplier Material materials with Hierro of 0.6 % | max., Nickel + Cobalt + Iron | |
Níquel | 0.2 % Show Supplier Material materials with Níquel of 0.2 % | min. Nickel + Cobalt | |
Plomo | 0.6 - 2 % Show Supplier Material materials with Plomo of 0.6 - 2 % | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Coaxial RF connectors and circular connectors and contact probes. This alloy to be fabricated into contacts for electronics, aircraft and automotive applications. | |
| General machinability | 60% (vs. free-cutting brass) | |