General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.27 g/cm³ Show Supplier Material materials with Densidad of 8.27 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Rockwell A | 23.0 °C | 39 - 57 [-] Show Supplier Material materials with Dureza Rockwell A of 39 - 57 [-] | |
Dureza Vickers | 23.0 °C | 106 - 200 [-] Show Supplier Material materials with Dureza Vickers of 106 - 200 [-] | |
Elongación | 23.0 °C | 30 % Show Supplier Material materials with Elongación of 30 % | min., for strip thicker than 0.10 mm |
Límite elástico Rp 0,2 | 23.0 °C | 280 - 480 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 280 - 480 MPa | |
Módulo elástico | 23.0 °C | 195 - 210 GPa Show Supplier Material materials with Módulo elástico of 195 - 210 GPa | |
Plegabilidad 90 ° bidireccional | 23.0 °C | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0 [-] | |
Plegabilidad 90 ° en peso bruto | 23.0 °C | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | |
Resistencia a la tracción | 23.0 °C | 660 - 900 MPa Show Supplier Material materials with Resistencia a la tracción of 660 - 900 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.45E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.45E-5 1/K |
Conductividad térmica | 23.0 °C | 48 W/(m·K) Show Supplier Material materials with Conductividad térmica of 48 W/(m·K) |
Temperatura de fusión | 1195 - 1325 °C Show Supplier Material materials with Temperatura de fusión of 1195 - 1325 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 23.0 °C | 4.31E-7 Ω·m Show Supplier Material materials with Resistividad eléctrica of 4.31E-7 Ω·m |
Specific Electrical conductivity | 4 % IACS Show Supplier Material materials with Specific Electrical conductivity of 4 % IACS |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Berilio | 1.85 - 2.05 % Show Supplier Material materials with Berilio of 1.85 - 2.05 % | ||
Cobre | 0.25 % Show Supplier Material materials with Cobre of 0.25 % | max. | |
Níquel | Balance |
Technological properties
Property | ||
---|---|---|
Application areas | Some applications for this alloy are Belleville washers for fire protection sprinkler heads, thermostats, bellows, diaphragms, connectors and burn-in and test sockets electrical /electronic systems. | |
Plating | Alloy 360 strip when properly cleaned exhibits surface chemistry characteristics similar to other commercial nickel base alloys. Techniques and procedures for plating and joining commercial nickel base alloys can be used on nickel beryllium. | |
Workability | Excellent - Used for deep-drawn and severely cupped or formed parts; can be bent flat through 180° angle in any direction |