General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.41 g/cm³ Show Supplier Material materials with Densidad of 8.41 g/cm³ |
Mecánica
Property | Temperature | Value |
---|---|---|
Dureza Rockwell B | 23.0 °C | 45 - 85 [-] Show Supplier Material materials with Dureza Rockwell B of 45 - 85 [-] |
Elongación | 23.0 °C | 35 - 60 % Show Supplier Material materials with Elongación of 35 - 60 % |
Límite elástico Rp 0,2 | 23.0 °C | 130 - 280 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 130 - 280 MPa |
Módulo elástico | 23.0 °C | 131 GPa Show Supplier Material materials with Módulo elástico of 131 GPa |
Resistencia a la tracción | 23.0 °C | 410 - 590 MPa Show Supplier Material materials with Resistencia a la tracción of 410 - 590 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 23.0 °C | 105 W/(m·K) Show Supplier Material materials with Conductividad térmica of 105 W/(m·K) |
Temperatura de fusión | 870 °C Show Supplier Material materials with Temperatura de fusión of 870 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 23.0 °C | 6.2E-6 - 7.89E-6 Ω·m Show Supplier Material materials with Resistividad eléctrica of 6.2E-6 - 7.89E-6 Ω·m |
Specific Electrical conductivity | 22 - 28 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 - 28 % IACS |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Berilio | 1.6 - 1.85 % Show Supplier Material materials with Berilio of 1.6 - 1.85 % | ||
Cobalto | 0.2 % Show Supplier Material materials with Cobalto of 0.2 % | min. Nickel + Cobalt | |
Cobre | Balance | ||
Hierro | 0.6 % Show Supplier Material materials with Hierro of 0.6 % | max., Nickel + Cobalt + Iron | |
Níquel | 0.2 % Show Supplier Material materials with Níquel of 0.2 % | min. Nickel + Cobalt |
Technological properties
Property | ||
---|---|---|
Application areas | Typical applications for parts finished by forging or extrusion of these alloys include undersea instrument and repeater housings, generator rings, and resistance welding components. |