General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.69 g/cm³ Show Supplier Material materials with Densidad of 8.69 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro exterior | 114.3 mm Show Supplier Material materials with Diámetro exterior of 114.3 mm | max., other sizes are available upon request |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell (HBW) | 23.0 °C | 265 [-] Show Supplier Material materials with Dureza Brinell (HBW) of 265 [-] | |
Dureza Rockwell C | 23.0 °C | 27 [-] Show Supplier Material materials with Dureza Rockwell C of 27 [-] | HRC values converted per ASTM-E-140, Table 1. |
Elongación | 23.0 °C | 7 % Show Supplier Material materials with Elongación of 7 % | |
Límite elástico Rp 0,2 | 23.0 °C | 790 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 790 MPa | |
Módulo elástico | 23.0 °C | 130 GPa Show Supplier Material materials with Módulo elástico of 130 GPa | |
Resistencia a la tracción | 23.0 °C | 860 MPa Show Supplier Material materials with Resistencia a la tracción of 860 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 25.0 °C | 155 W/(m·K) Show Supplier Material materials with Conductividad térmica of 155 W/(m·K) |
250.0 °C | 215 W/(m·K) Show Supplier Material materials with Conductividad térmica of 215 W/(m·K) | |
Chemical properties
Property | Value |
---|---|
Cobre | Balance |
Cromo | 0.6 - 1.2 % Show Supplier Material materials with Cromo of 0.6 - 1.2 % |
Níquel | 6.4 - 6.7 % Show Supplier Material materials with Níquel of 6.4 - 6.7 % |
Silicona | 1.5 - 2.5 % Show Supplier Material materials with Silicona of 1.5 - 2.5 % |
Technological properties
Property | ||
---|---|---|
Application areas | Applications include valve seats, valve guides, piston rings and plain bearings, where PerforMet provides long life while efficiently removing heat from critical engine components. |