Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 8.36 g/cm³ Show Supplier Material materials with Densidad of 8.36 g/cm³ |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Rockwell C | 23.0 °C | 30 [-] Show Supplier Material materials with Dureza Rockwell C of 30 [-] | |
Elongación | 23.0 °C | 15 % Show Supplier Material materials with Elongación of 15 % | |
Energía de impacto Charpy | 23.0 °C | 20 J Show Supplier Material materials with Energía de impacto Charpy of 20 J | |
Límite elástico Rp 0,2 | 23.0 °C | 760 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 760 MPa | |
Módulo elástico | 23.0 °C | 131 GPa Show Supplier Material materials with Módulo elástico of 131 GPa | |
Resistencia a la fatiga | 23.0 °C | 310 MPa Show Supplier Material materials with Resistencia a la fatiga of 310 MPa | 10⁷ cycles, R=-1 |
Resistencia a la tracción | 23.0 °C | 965 MPa Show Supplier Material materials with Resistencia a la tracción of 965 MPa |
Aplicaciones térmicas
| Property | Temperature | Value |
|---|---|---|
Calor específico | 100.0 °C | 420 J/(kg·K) Show Supplier Material materials with Calor específico of 420 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.75E-5 1/K |
Conductividad térmica | 100.0 °C | 155 W/(m·K) Show Supplier Material materials with Conductividad térmica of 155 W/(m·K) |
Temperatura de fusión | 870 °C Show Supplier Material materials with Temperatura de fusión of 870 °C |
Chemical properties
| Property | Value |
|---|---|
Berilio | 1.6 - 2 % Show Supplier Material materials with Berilio of 1.6 - 2 % |
Cobalto | 0.2 - 0.3 % Show Supplier Material materials with Cobalto of 0.2 - 0.3 % |
Cobre | Balance |
Technological properties
| Property | ||
|---|---|---|
| Application areas | MoldMAX LH alloy is used for injection mold cores and cavities where moderate hardness and high toughness and conductivity are required. | |