Propiedades
General
| Property | Value |
|---|---|
Densidad | 8.7 g/cm³ Show Supplier Material materials with Densidad of 8.7 g/cm³ |
Medidas
| Property | Value |
|---|---|
Dimensions | Strip thickness 0.08 - 3.0 mm, other gauges on request. Strip width from 8.5 mm. |
Mecánica
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Coeficiente de Poisson | 0.33 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.33 [-] | ||
Dureza Vickers | 90 - 120 [-] Show Supplier Material materials with Dureza Vickers of 90 - 120 [-] | R375(O) | For reference only | |
120 - 180 [-] Show Supplier Material materials with Dureza Vickers of 120 - 180 [-] | R440(H/2) | For reference only | ||
150 - 210 [-] Show Supplier Material materials with Dureza Vickers of 150 - 210 [-] | R540(H) | For reference only | ||
185 [-] Show Supplier Material materials with Dureza Vickers of 185 [-] | min. | R610(EH) | For reference only | ||
Elongación | 20 % Show Supplier Material materials with Elongación of 20 % | min. | R375(O), A50 | |
Límite elástico | 180 MPa Show Supplier Material materials with Límite elástico of 180 MPa | min. | R375(O) | |
250 MPa Show Supplier Material materials with Límite elástico of 250 MPa | min. | R440(H/2) | ||
420 MPa Show Supplier Material materials with Límite elástico of 420 MPa | min. | R540(H) | ||
520 MPa Show Supplier Material materials with Límite elástico of 520 MPa | min. | R610(EH) | ||
Módulo elástico | 135 GPa Show Supplier Material materials with Módulo elástico of 135 GPa | ||
Plegabilidad 180 ° bidireccional | 0 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 0 [-] | ASTM B820 | R375(O) | bending thickness: 0.08-0.2 mm & bending width: 10 mm |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 2 [-] | ASTM B820 | R440(H/2) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
4 [-] Show Supplier Material materials with Plegabilidad 180 ° bidireccional of 4 [-] | ASTM B820 | R540(H) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
Plegabilidad 180 ° en peso bruto | 0 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 0 [-] | ASTM B820 | R375(O) | bending thickness: 0.08-0.2 mm & bending width: 10 mm |
0 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 0 [-] | ASTM B820 | R440(H/2) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
2 [-] Show Supplier Material materials with Plegabilidad 180 ° en peso bruto of 2 [-] | ASTM B820 | R540(H) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
Plegabilidad 90 ° bidireccional | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 0 [-] | EN ISO 7438 | R375(O) | bending thickness: 0.08-0.2 mm & bending width: 10 mm |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 1 [-] | EN ISO 7438 | R440(H/2) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
3 [-] Show Supplier Material materials with Plegabilidad 90 ° bidireccional of 3 [-] | EN ISO 7438 | R540(H) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
Plegabilidad 90 ° en peso bruto | 0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | EN ISO 7438 | R375(O) | bending thickness: 0.08-0.2 mm & bending width: 10 mm |
0 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 0 [-] | EN ISO 7438 | R440(H/2) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
1 [-] Show Supplier Material materials with Plegabilidad 90 ° en peso bruto of 1 [-] | EN ISO 7438 | R540(H) | bending thickness: 0.08-0.2 mm & bending width: 10 mm | |
Resistencia a la tracción | 440 - 570 MPa Show Supplier Material materials with Resistencia a la tracción of 440 - 570 MPa | R440(H/2) | |
540 - 640 MPa Show Supplier Material materials with Resistencia a la tracción of 540 - 640 MPa | R540(H) |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 340 J/(kg·K) Show Supplier Material materials with Calor específico of 340 J/(kg·K) | ||
Coeficiente de dilatación térmica | 1.68e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.68e-05 1/K | average value between 20-300°C | |
Conductividad térmica | 20 °C | 32 W/(m·K) Show Supplier Material materials with Conductividad térmica of 32 W/(m·K) |
Eléctrico
Chemical properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Application target: Ideal for EMI shielding ,gaskets etc. | |
| Chemical composition | The chemical composition is the nominal composition of the alloy | |
| Coating | Electroplating: Very good Hot dip tinning: Very good | |
| Cold Forming | Very good | |
| Machining | Less Suitable | |
| Packaging size | Standard coils with outside diameters up to 1300 mm. Traverse-wound coils with drum weights up to 500 kg. Multiple-coil up to 3 tons. | |
| Soldering general | Soft soldering: Very good | |
| Testings | Fatigue strength: The fatigue strength is defined as the maximum bending stress amplitude which a material withstands for 10.000.000 load cycles under symmetrical alternate load without breaking. It depends on the temper selected and can be estimated typically by 1/3 of tensile strength. For solid solution fine grain materials fatigue strength might increase up to 0,5 * of tensile strength. Bending test: 90° bend test According to EN ISO 7438, 180° bend test acc. to ASTM B820, shown values might show orange- peel, however no crack. | |
| Welding | Laser welding: Good Resistance welding: Very good | |