General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.1 g/cm³ Show Supplier Material materials with Densidad of 1.1 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.12 [-] Show Supplier Material materials with Densidad relativa of 1.12 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.42 % Show Supplier Material materials with Moisture absorption of 0.42 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 6.1 % Show Supplier Material materials with Elongación of 6.1 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 88 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 88 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2290 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2290 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 2.7 GPa Show Supplier Material materials with Módulo elástico of 2.7 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 106 MPa Show Supplier Material materials with Resistencia a la flexión of 106 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 77 MPa Show Supplier Material materials with Resistencia a la tracción of 77 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 230 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 230 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.7E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9.1E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature, 0.45 MPa | 120 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 120 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 109 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 109 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 109 - 120 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 109 - 120 °C | ||
Temperatura de reblandecimiento Vicat | 169 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 169 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.78 % Show Supplier Material materials with Contracción of 0.78 % | ISO 294 | 24 hrs |
Contracción transversal | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción transversal of 1.1 % | ISO 294 | 24 hrs |
Velocidad de flujo del volumen derretido | 1.04 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 1.04 cm³/10min | ISO 1133 | MVR at 330°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Recreational Vehicle, Data Management, Auto Electrical, Engine Component | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |