Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of friction | 0.33 [-] Show Supplier Material materials with Coefficient of friction of 0.33 [-] | ||
Coefficient of friction, kinetic | 0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.12 g/cm³ Show Supplier Material materials with Densidad of 1.12 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 5 % Show Supplier Material materials with Elongación of 5 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 463 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 463 J/m | ASTM D 256 | notched, -30°C |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Supplier Material materials with Módulo de flexión of 2.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo elástico of 2.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la tracción | 23.0 °C | 50 MPa Show Supplier Material materials with Resistencia a la tracción of 50 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 49 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 49 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 40 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 208 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 208 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 0.45 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 125 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 104 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 104 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Temperatura de flexión bajo carga | 104 - 125 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 104 - 125 °C | |
Temperatura de reblandecimiento Vicat | 124 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 124 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.7 % Show Supplier Material materials with Contracción of 0.7 % | SABIC method |
Contracción transversal | 23.0 °C | 0.8 % Show Supplier Material materials with Contracción transversal of 0.8 % | SABIC method |
Velocidad de flujo de la masa derretida | 23 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 23 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 21 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 21 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive , Console, Infotainment/Telematic, Interior, Interior trims | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 105 to 110.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |